Technology Equipment and Production Practice for CSP Concasting and Continuous Rolling Process at Lianyuan Steel

吴光亮; 郑柏平; 焦国华; 周明伟; 罗刚

您当前的位置：

首页 >

文章列表页 >

Technology Equipment and Production Practice for CSP Concasting and Continuous Rolling Process at Lianyuan Steel

更新时间：2026-01-21

- Technology Equipment and Production Practice for CSP Concasting and Continuous Rolling Process at Lianyuan Steel
- Special Steel Vol. 27, Issue 2, Pages: 46-48(2006)
- 作者机构：
  
  1. 涟源钢铁集团有限公司,娄底,417009
  2. 钢铁研究总院,北京,100081
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：13 October 2005，
  
  Online First：02 March 2023，
  
  Published：02 March 2006
- 稿件说明：
移动端阅览
吴光亮, 郑柏平, 焦国华, et al. Technology Equipment and Production Practice for CSP Concasting and Continuous Rolling Process at Lianyuan Steel[J]. Special Steel, 2006, 27(2): 46-48.
DOI：

吴光亮, 郑柏平, 焦国华, et al. Technology Equipment and Production Practice for CSP Concasting and Continuous Rolling Process at Lianyuan Steel[J]. Special Steel, 2006, 27(2): 46-48. DOI：

摘要

涟钢CSP连铸连轧流程为SMS-DEMAG公司的第2代CSP技术。主要流程为3×100 t顶底复吹转炉-3×100 t钢包炉(LF)-2流4555 mm CSP连铸-辊底式均热炉-7架连轧机。该生产线2004年投产

预计2005年产量超过270万t。简要分析和介绍了涟钢CSP流程的装备、技术特性和生产实践

并提出进一步挖掘涟钢CSP流程潜力的技术思路。

Abstract

The CSP concasting and continuous rolling flow sheet at Lianyuan Steel is second generation CSP technology of SMS-DEMAG

of which the main process is 3×100 t top and bottom combined blown converters- 3×100 t ladle fumaccs (LF)- two strand 45~55 mm thin slab CSP concasting-roller-hearth pit soaking furnace - 7-stand continuous rolling mill. The production line was put into production in 2004

and predicted annual output in 2005 shall be more than 2.7×10⁶t. The equipment

technical characteristics and production practice of CSP process at Lianyuan Steel are analyzed and present- ed

and the technology idea for further tapping CSP process potential at Lianyuan Steel is put forward.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Production Practice of Continuous Casting of Φ500 mm Heavy Round Bloom

Productive Practice of Refining with a 300 t RH Unit for IF Steel

Production Practice of Φ600 mm Round Bloom of HSLA Steel Q345E

Production Practice and Analysis on Two-Step and Three-Step Process for Stainless Steels Steelmaking

Practice of Pilot Production on Φ350 mm Cast Round Bloom of Steel 4130 by 50 t EAF-LF (VD)-CC Flow Sheet

Related Author

张志宏

刘伟平

李国光

成国光

王社教

倪红卫

尹修刚

陈宏豫

Related Institution

北京科技大学冶金与生态工程学院

承德建龙特殊钢有限公司

武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室

山西太钢不锈钢股份有限公司技术中心

山东钢铁股份有限公司莱芜分公司特钢事业部

⁰