- Effect of Slag Ingredient on Ti Burning Loss Rate and Ingot Surface Quality of High Temperature Alloy 0Cr15Ni25Ti2MoAlVB
- Special Steel Vol. 27, Issue 2, Pages: 61-62(2006)
- 作者机构：
  
  太原钢铁(集团)公司技术中心,太原,030003
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：15 November 2005，
  
  Online First：02 March 2023，
  
  Published：02 March 2006
- 稿件说明：
移动端阅览
赵鸿燕. Effect of Slag Ingredient on Ti Burning Loss Rate and Ingot Surface Quality of High Temperature Alloy 0Cr15Ni25Ti2MoAlVB[J]. Special Steel, 2006, 27(2): 61-62.
DOI：

赵鸿燕. Effect of Slag Ingredient on Ti Burning Loss Rate and Ingot Surface Quality of High Temperature Alloy 0Cr15Ni25Ti2MoAlVB[J]. Special Steel, 2006, 27(2): 61-62. DOI：

摘要

试验分析了2.5 t电渣炉使用4种成分熔渣重熔0Cr15Ni25Ti2MoAlVB合金时的Ti烧损率。试验结果表明

4种渣系中75%CaF

-15%Al

-10%CaO三元提纯渣的Ti烧损率最低

为7.0%

并且避免了70%CaF

-30%Al

的二元渣系重熔钢锭表面渣沟等缺陷。

Abstract

Ti burning loss rate during electroslag remelting(ESR)of alloy 0Cr15Ni25Ti2MoAlVB in a 2.5 t ESR furnace by 4 kinds of slag systems was tested and analyzed.The test results showed that as remelting using 75%CaF

-15%Al

-10%CaO pure terary slag the Ti burning loss rate was 7.0%

lowest in 4 slag systems and free slag groove of ingot surface which occurred as remelting using 70%CaF

-30%Al

binary slag.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Electromagnetic Stirring on Temperature Field of ESR Ingot

Control of Carbon and Sulfur Content in Electroslag Remelting Pure Iron

A Study on Evaporation of Fluorides in Slag during Electroslag Remelting Process

Analysis on Internal Cracks in Fe-Cr-Al Alloy Electroslag Remelting Ingot and Improved Process Measure

Effect of Argon Shielding Atmosphere on Burning Loss of Titanium in Steel lCrl8Ni9Ti in Electro-Slag Remelting Process

Related Author

厉英

李宝宽

白海军

赵昱臻

任学平

包卫平

王新宇

苗晓

Related Institution

东北大学材料与冶金学院

北京科技大学材料科学与工程学院

太钢不锈钢股份有限公司技术中心

西安建筑科技大学冶金工程学院

北京科技大学冶金与生态工程学院

⁰