Effect of Cold Rolling and Solid Solution Treatment on Structure and Mechanical Properties of Modified Type 202 Stainless Steel

范植金; 黄静; 李洪波; 许文启; 汤小兰

您当前的位置：

首页 >

文章列表页 >

Effect of Cold Rolling and Solid Solution Treatment on Structure and Mechanical Properties of Modified Type 202 Stainless Steel

更新时间：2026-01-21

- Effect of Cold Rolling and Solid Solution Treatment on Structure and Mechanical Properties of Modified Type 202 Stainless Steel
- Special Steel Vol. 27, Issue 2, Pages: 17-19(2006)
- 作者机构：
  
  1. 武钢集团技术中心,武汉,430080
  2. 武钢集团海南公司,海口,571924
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：07 October 2005，
  
  Online First：24 February 2023，
  
  Published：24 February 2006
- 稿件说明：
移动端阅览
范植金, 黄静, 李洪波, et al. Effect of Cold Rolling and Solid Solution Treatment on Structure and Mechanical Properties of Modified Type 202 Stainless Steel[J]. Special Steel, 2006, 27(2): 17-19.
DOI：

范植金, 黄静, 李洪波, et al. Effect of Cold Rolling and Solid Solution Treatment on Structure and Mechanical Properties of Modified Type 202 Stainless Steel[J]. Special Steel, 2006, 27(2): 17-19. DOI：

摘要

研究总冷轧变形量12.5%～46.4%和900～1150℃固溶处理对成分(%)为:0.04C

8.18Mn

15.21Cr

4.05Ni

1.65Cu

0.12N的改进型202亚稳奥氏体不锈钢3 mm板组织和性能的影响。结果表明

经总变形量46.4%冷轧后

形变诱发产生约26%α′马氏体

该钢的强度达1200 MPa;固溶处理使α′马氏体发生逆转变(α′→γ)

900℃固溶可使α′马氏体完全转变成γ奥氏体并完成全部再结晶;改进型不锈钢经900～1100℃固溶处理具有预期的组织和良好的综合力学性能。

Abstract

The effect of total reduction ratio 12.5%～46.4% and solid solution treatment at 900~1150 ℃ on the structure and pmoperties of 3 mm sheet of a modifed type 202 metastable austenite stainless steel- 0.04C

8.18Mn

15.21Cr

4.05Ni

1.65Cu

0.12N has been studied. The results showed that with 46.4% reduction cold rolling

about 26% deformation-induced a' martensite was formed and the tensile strength of the steel was up to 1200 MPa; the counter- transformation of a' martensite(a' to γ)occured by solid solution treatment

and with solid solution at 900 ℃ the a' mar- tensite was completely transformmed to γ austenite and the full recrystallization of stcel was finished; and the expected structure and excellent comprehensive mechanical properties were obtainad by solid solution treatment at 900~1100 ℃.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Structure and Properties of Coarse Grain Heat Affected Zone of Zr Microalloying HSLA Steel

Effect of Deformation on Structure and Mechanical Properties of Non-Orientation Silicon Steel 50W470

An Analysis on Strengthening Factors and Mechanical Properties of Q345B Steel Strip Produced by CSP Process

Effect of Annealing Process on Structure and Properties of 0.17C Cold Rolled Steel Sheet for Chain

Hot Rolling and Properties of 304/440/304 Stainless Steels Clad Plate for Knife Products

Related Author

习天辉

陈晓

陈颜堂

浦绍康

孙述利

郭东城

刘江

宋文军

Related Institution

武汉钢铁(集团)公司技术中心

太原科技大学材料学院

太原钢铁有限公司

武汉科技大学材料与冶金学院

华中科技大学材料学院

⁰