With  using  60%  hot  metal  +  quality  scrap  charge

Consteel  EAF  eccentric  bottom  tapping  operation

con- trolling    tapping    end [C

]

    0.035%～0.050%    and    tapping[P

]

≤0.012%

LF    refining    by    low    basicity    slag

feeding silicon  wire

  soft  blown  argon  for  15  min  after  LF  refining  and  fully  shielding  auto  control  casting  150  mmx150  mm  bilet  in whole period

  the  average oxygen  content  in steel  H11Mn2SiA(0.06~0.09C

0.82～1.00Si

1.45~1.70Mn)for welding  wire  was  20×10

-6

of which  the  Φ5.5  mm  wire  rods  could  be  direct  drawn  to  φ1.0  mm  wire  without  by  heat  treatment and  no-broken  wire   occurred.