Effect of Heat Treatment on Structure and Mechanical Properties of Spring Steel 60Si2CrVAT

王凯; 殷匠; 顾文俊; 胡俊辉

您当前的位置：

首页 >

文章列表页 >

Effect of Heat Treatment on Structure and Mechanical Properties of Spring Steel 60Si2CrVAT

更新时间：2026-01-21

- Effect of Heat Treatment on Structure and Mechanical Properties of Spring Steel 60Si2CrVAT
- Special Steel Vol. 28, Issue 6, Pages: 56-58(2007)
- 作者机构：
  
  宝钢股份有限公司特殊钢分公司,上海,200940
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：18 May 2007，
  
  Online First：29 December 2022，
  
  Published：29 December 2007
- 稿件说明：
移动端阅览
王凯, 殷匠, 顾文俊, et al. Effect of Heat Treatment on Structure and Mechanical Properties of Spring Steel 60Si2CrVAT[J]. Special Steel, 2007, 28(6): 56-58.
DOI：

王凯, 殷匠, 顾文俊, et al. Effect of Heat Treatment on Structure and Mechanical Properties of Spring Steel 60Si2CrVAT[J]. Special Steel, 2007, 28(6): 56-58. DOI：

摘要

试验了890～930℃淬火、400～440℃回火时淬-回火温度对160mm×160mm连铸坯轧成的Φ21mm 60Si2CrVAT弹簧钢组织和力学性能的影响。结果表明

910℃淬火.回火后的60Si2CrVAT钢抗拉强度高于890℃和930℃淬火-回火钢的抗拉强度

不同淬火温度下钢的抗拉强度随回火温度升高而降低。分析了拉伸断口的组织形貌。

Abstract

The effect of quenching and tempering temperature of Φ21 mm finished products rolled by 160 mm×160 mm concasting billet of spring steel 60Si2CrVAT quenched at 890~930 ℃ and tempered at 400～440 ℃ on structure and mechanical properties of steel has been tested. Results showed that the tensile strengh of tempered spring steel 60Si2CrVAT quenched at 910 ℃ was higher than that quenched at 890 ℃ and 930 ℃

and with increasing tempering tem perature the tensile strength of steel quenched at different temperature decreased. The structure morphology of tensile frac ture was analyzed.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Heat Treatment Process on Microstructure and Properties of Forged 430F Ferritic Stainless Steel

Effect of Heat Treatment Temperature on Microstructure and Properties of 0Cr21Al6 Hot Rolled Sheet

Effect of Heat Treatment Regime on Mechanical Properties and Microstructure of 0.37C-0.6Mn-0.82Cr Steel

Effect of Forging Process on Microstructure and Properties of Fe10Cr10Co Soft Magnetic Alloy

Development of M42 and above 12.9 Grade High Hardenability 42CrMoVNb Bolt Steel

Related Author

Xu Linchao

Ye Sainan

Wang Wenquan

Zhang Xinge

Lu You

Guo Wei

Gao Peijun

Yang Mi

Related Institution

College of Optoelectronic Manufacturing， Zhe Jiang Industry & Trade Vocational College

School of Material Science and Engineering，Jilin University

Shanxi Taiyuan Stainless Co.， Ltd.

Taiyuan University of Technology

Shanghai Aerospace Equipments Manufacturer Co.， Ltd.

⁰