Main     advances     in     0.03～0.05C

2.80～3.40Si     cold     rolled     grain-oriented     electrical     steels     are     presented including   obvious   improvement   of  magnetic   properties   by   improving   texture

   decreasing   thickness   of   sheet   and   using   magnetic   domain   refining   techniques;   research   on   mechanism   of   secondary   recrystallization   texture   selecting   growth   and   Goss   texture   forming;   and   low   temperature   reheating   technology   for   slab   and   compact   flow   sheet   process   etc.