Non-Metallic Inclusion in Grade A Hull Plate Steel Produced by 30 t Converter-Ladle Argon Stirring -Concasting Flowsheet

尚德礼; 张洪哲; 吕春风

您当前的位置：

首页 >

文章列表页 >

Non-Metallic Inclusion in Grade A Hull Plate Steel Produced by 30 t Converter-Ladle Argon Stirring -Concasting Flowsheet

更新时间：2026-01-21

- Non-Metallic Inclusion in Grade A Hull Plate Steel Produced by 30 t Converter-Ladle Argon Stirring -Concasting Flowsheet
- Special Steel Vol. 28, Issue 6, Pages: 51-53(2007)
- 作者机构：
  
  1. 鞍钢股份有限公司技术中心,鞍山,114009
  2. 河北理工大学冶金与能源学院,唐山,063009
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：22 May 2007，
  
  Online First：28 December 2022，
  
  Published：28 December 2007
- 稿件说明：
移动端阅览
尚德礼, 张洪哲, 吕春风. Non-Metallic Inclusion in Grade A Hull Plate Steel Produced by 30 t Converter-Ladle Argon Stirring -Concasting Flowsheet[J]. Special Steel, 2007, 28(6): 51-53.
DOI：

尚德礼, 张洪哲, 吕春风. Non-Metallic Inclusion in Grade A Hull Plate Steel Produced by 30 t Converter-Ladle Argon Stirring -Concasting Flowsheet[J]. Special Steel, 2007, 28(6): 51-53. DOI：

摘要

用电解法和扫描电镜(SEM)分析研究30t顶吹氧气转炉-钢包吹氩-150mm×1050mm板坯连铸工艺生产的A级船板钢(%:0.16C、0.21Si、0.50Mn、0.011P、0.027S)中的非金属夹杂的组成、尺寸、数量和分布。结果表明

A级船板钢中的夹杂物包括硅酸盐、铝硅酸盐、硫化物以及铝硅酸盐-硫化物复合夹杂物。钢水二次氧化及耐火材料外来夹杂抵消了吹氩去除夹杂物的冶金效果。增强中间包去夹杂能力可减少钢中大尺寸夹杂物。

Abstract

The compound

size

amount and distrbution of non-metallic inclusion in grade A hull plate steel (0. 16C

0.21Si

0.50Mn

0.011P

0.027S)produced by 30 t LD converter -ladle argon stiring- 150 mm×1050 mm slab concasting flowsheet have been analyzed and studied by electrolytic extraction analysis and scanning electron micro scope(SEM).Results showed that the inclusion in grade A hull plate stcel included silicate

alumina-silicate

sulphide and alumina-silicate-sulphide compound inclusion. The secondary oxidation of liquid steel and inclusion in steel from refractory materials counteract the metallurgical effect of argon blowing to remove inclusion in steel therefore to strengthen the ability of tundish removing inclusions could decrease large size inclusions in steel.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Failure Behavior of Ultra-high Cycle Fatigue of a 2 000 MPa Grade High Strength Steel

Effect of Adding AlzO3Nano-powder on Mechanical Properties and Inclusions of Hollow Steel 55SiMnMo

Development of Gear Steel 16MnCr5 by 40 % Hot Metal-50 t EAF-LF-VD-CC Flowsheet

Related Author

赵海民

陈思联

郝立群

惠卫军

董瀚

翁宇庆

王国承

黄浪

Related Institution

钢铁研究总院先进钢铁材料技术国家工程研究中心

云南大学

中国金属学会

北京科技大学冶金与生态工程学院

新余钢铁公司

⁰