Progress in Study on Precipitation Strengthening of Nb ( C, N) in Ferrite of Niobium Microalloying HSLA Steel

韦青峰

您当前的位置：

首页 >

文章列表页 >

Progress in Study on Precipitation Strengthening of Nb ( C, N) in Ferrite of Niobium Microalloying HSLA Steel

更新时间：2026-01-21

- Progress in Study on Precipitation Strengthening of Nb ( C, N) in Ferrite of Niobium Microalloying HSLA Steel
- Special Steel Vol. 28, Issue 5, Pages: 42-44(2007)
- 作者机构：
  
  攀枝花钢铁研究院材料所,攀枝花,617000
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：12 April 2007，
  
  Online First：14 February 2023，
  
  Published：14 February 2007
- 稿件说明：
移动端阅览
韦青峰. Progress in Study on Precipitation Strengthening of Nb ( C, N) in Ferrite of Niobium Microalloying HSLA Steel[J]. Special Steel, 2007, 28(5): 42-44.
DOI：

韦青峰. Progress in Study on Precipitation Strengthening of Nb ( C, N) in Ferrite of Niobium Microalloying HSLA Steel[J]. Special Steel, 2007, 28(5): 42-44. DOI：

摘要

介绍了含微量铌的高强度低合金(HSLA)钢铁素体中Nb(C

N)析出的数学模型

以及计算经900～1200℃奥氏体化处理后的铁素体中NbC形核半径、形核率和形核长大率。一些研究者的试验结果表明

Nb的碳氮化物在铁素体上的析出需要较高的位错密度

与奥氏体中形成的NbC相比较

铁素体中形成的NbC相对较少

在680℃卷取钢板的抗拉强度较未经卷取直接空冷至室温的钢板抗拉强度有明显提高。

Abstract

Mathematical model for Nb( C

N) precipitation in ferrite of micro niobium HSLA steel and calculated NbC nucleation radius

nucleation rate and growth rate in ferrite with 900 ~ 1200 ℃. austenization are presented. The test results by some authors indicated the precipitation of niobium carbo-nitride needed higher dislocation density and the amount of NbC formed in ferrite was relatively minor as compared with that formed in austenite； and the tensile strength of steel sheet with coiled at 680 °C was obviously higher than that of sheet without coiled direct cooling to room temperature.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Cold Drawing Deformation on Grain Size and Decarbonization Determination of 30CrMnSiNi2A Hexagonal Products

Effect of Salt Bath Isothermal Heat Treatment on Structure and properties of Ultra High Strength Hard Wire 100Si Steel

Calculation of Specific Interfacial Energy and Ripening Rate for Cooper in Ferrite of Bainite Steel

High Temperature Properties of Slab of Stainless Steels and Application in Concasting Secondary Cooling Process

Process Practice for Improving Fatigue Life of Steel 60Si2MnA for Auto Stabilizing Rod

Related Author

Zhao Chengzhi

Zhang Yuchun

Li Jianxin

Pang Xuedong

Sun Yong

ZhaiYujia

Liang Xiaodong

Xu Kai

Related Institution

Technology Center， Fushun Special Steel Co.， Ltd.

Research Institute of Wire Materials， Qingdao Special Steel Co.， Ltd.

Railway Construction Institute， China Academy of Railway Sciences

云南大学材料系

钢铁研究总院先进钢铁流程及材料国家重点实验室

⁰