Control Process on Corner Crack of 200 mm×200 mm Hot Rolled Billet of Steel 34Mn2V for High Pressure Bottle

陈永; 杨素波; 朱苗勇

您当前的位置：

首页 >

文章列表页 >

Control Process on Corner Crack of 200 mm×200 mm Hot Rolled Billet of Steel 34Mn2V for High Pressure Bottle

更新时间：2026-01-21

- Control Process on Corner Crack of 200 mm×200 mm Hot Rolled Billet of Steel 34Mn2V for High Pressure Bottle
- Special Steel Vol. 29, Issue 6, Pages: 28-30(2008)
- 作者机构：
  
  1. 东北大学材料与冶金学院,沈阳,110004
  2. 攀枝花钢铁研究院,攀枝花,617000
  3. 攀枝花新钢钒股份有限公司提钒炼钢厂,攀枝花,617062
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：07 May 2008，
  
  Online First：07 December 2022，
  
  Published：07 December 2008
- 稿件说明：
移动端阅览
陈永, 杨素波, 朱苗勇. Control Process on Corner Crack of 200 mm×200 mm Hot Rolled Billet of Steel 34Mn2V for High Pressure Bottle[J]. Special Steel, 2008, 29(6): 28-30.
DOI：

陈永, 杨素波, 朱苗勇. Control Process on Corner Crack of 200 mm×200 mm Hot Rolled Billet of Steel 34Mn2V for High Pressure Bottle[J]. Special Steel, 2008, 29(6): 28-30. DOI：

摘要

通过工艺对比分析了34Mn2V高压气瓶用钢中间包浇铸温度、结晶器液面波动、[Als]、中问包炉次和280 mm×380 mm连铸坯拉速波动对轧坯角部拉裂的影响。提出减小RH加Al量

按[Als]0.01%控制;RH后喂Ca-Si线;适当提高连铸钢液温度

控制中间包钢水温度1 520～1 530℃;控制浇铸过程塞棒吹氩量≤10 L/min;结晶器液位波动±3 mm等工艺措施。应用结果表明

轧坯角部拉裂缺陷率由原来的23.57%降至1.21%。

Abstract

The effect of temperature of liquid steel in tundish during casting

liquid level fluctuation in mold

[Als]

sequence heats of tundish and fluctuation of 280 mm×380 mm bloom casting speed on rolled billet comer cracks of steel 34Mn2V for high pressure bottle was analyzed by processes comparison. The process measures have been adopted including decreasing adding Al amount

controlling[Als]0.01%

feeding Ca-Si wire after RH

suitably increasing liquid steel temperature during cast

controlling liquid steel temperature 1520～1530 ℃ in tundish and stopper argon blown rate ≤10 L/min during casting

and controlling mold liquid level fluctuation ±3 mm.Application results showed that the hot rolled billet comer cracks rate decreased from original 23.57% to 1.21%.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Controlling Technology on Oxygen Content in Gear Steel Produced by 120 t LD-LF-RH-BCC Flow Sheet

Analysis on Formation of Outer Fold of 37Mn5 Steel Tube and Process Control

Physical Simulation of Liquid Flow Field in 45 t Tundish for Four Strand Bloom and Its Metallurgical Effect

Related Author

曾建华

王新华

赵克文

杨素波

陈天明

洪慧平

康永林

李春雨

Related Institution

攀枝花钢铁集团公司

北京科技大学冶金与生态工程学院

北京科技大学材料科学与工程学院

中冶连铸北京冶金技术研究院

湖北新冶钢有限公司炼钢事业部转炉分厂

⁰