Rolling        test        on        steel        plate(0.09C

0. 12Si

0.98Mn

0.010P

0.005S

0.010Nb

0.04Als)for        wheel spoke  with  finishing  rolling  temperature  830～890  ℃  and  coiling  temperature  620～680  ℃  has  been  carried  out  by 1700mm  hot  rolling  mill  train.  Results  showed  that  with  slab  heating  temperature  1230~1250  ℃

finishing  rolling  tem- perature  870±15℃

coiling  temperature  660±15  ℃

the  structure  of  steel  plate  for  wheel  spoke  was  fine  ferrite  +  minor pearlite

the   yield   strength   of   steel   was   335～380MPa

tensile   strength   430～485MPa

elongation   26%~31%

the   longitudinal  strength  difference  of each  steel  coil  was  13~37MPa

and  the  punching  formability  during  vehicle  wheel  manufacturing  was  excellent  with  punching  rejection  rate  less  than  0.3%.