Influence of Pulse Current Treatment Method on Solidified Structure of a 45 Steel

张西锋; 袁守谦; 魏颖娟; 邱斌; 杨拉道; 谢东钢

您当前的位置：

首页 >

文章列表页 >

Influence of Pulse Current Treatment Method on Solidified Structure of a 45 Steel

更新时间：2026-01-21

- Influence of Pulse Current Treatment Method on Solidified Structure of a 45 Steel
- Special Steel Vol. 30, Issue 1, Pages: 10-12(2009)
- 作者机构：
  
  1. 西安建筑科技大学冶金工程学院,西安,710055
  2. 西安重型机械研究所,西安,710032
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：10 July 2008，
  
  Online First：29 November 2022，
  
  Published：29 November 2009
- 稿件说明：
移动端阅览
张西锋, 袁守谦, 魏颖娟, et al. Influence of Pulse Current Treatment Method on Solidified Structure of a 45 Steel[J]. Special Steel, 2009, 30(1): 10-12.
DOI：

张西锋, 袁守谦, 魏颖娟, et al. Influence of Pulse Current Treatment Method on Solidified Structure of a 45 Steel[J]. Special Steel, 2009, 30(1): 10-12. DOI：

摘要

45钢(0.43%C)在10kg中频感应炉出钢前(凝固前)经2600V、0.862Hz、电容器电容量200μF脉冲电流处理60s和钢水在铸模凝固过程用相同参数的脉冲电流处理3.5min后发现

两种脉冲电流处理方法均能改善钢的凝固组织:增加等轴晶和减少柱状晶数量

并减少魏氏组织

使珠光体片层间距减小;同时改善了钢的成分偏析

碳、硫、磷的偏析指数分别由未经脉冲电流处理的1.257、1.502和1.384降低至脉冲电流处理的1.125～1.194、1.067～1.300、1.227～1.092。

Abstract

With pulse current ( 2 600 V

0. 862 Hz

capacitance of capacitor 200 μF) treated liquid 45 steel (0. 43% C) for 60 s before tapping from 10 kg medium frequency furnace ( before solidification) or with same pulse current treated liquid for 3. 5 min during solidified process in casting mold

it was found that both pulse current treated methods all were able to improve solidified structure of steel

i. e. increased equiaxial crystal

decreased columnar crystal. reduced Widmannstattern structure and decreased interlamellar spacing of pearlite

besides to improve chemical composition segregation

the segregation index of carbon

sulphur and phosphorus respectively decreased to 1. 125 ~ 1. 194

1. 067 ~ 1. 300 and 1. 227 ~ 1. 092 with pulse current treatment from 1. 257

1. 502 and 1. 384 without pulse current treatment.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preventive Measures of Widmanstatten Structure of 0.45 % C Steel for Automobile Piston Rod and Process Optimization

Simulation Study and Application on Solidification Structure of E36 Steel Ship Slab

Analysis and Control on Center Cracks of Rectangular Billet of 45C Steel

A Study on Friction and Wear Behavior of Low Temperature Electrolytic Sulphurizing Surface of 0.45C Steel<

Effect of Magnesium Treatment on Inclusion Formation and Solidification Structure Ferrite Stainless Steel 430

Related Author

李合意

王毅

杨浩

任建忠

吴豪明

曾凡政

卢欣欣

李曜光

Related Institution

河南济源钢铁(集团)有限公司

北京科技大学钢铁共性技术协同创新中心

湖南华菱湘潭钢铁有限公司

北京科技大学1冶金工程研究院

冶金与生态工程学院

⁰