Hot Ductility of Continuous Casting Billet of 10B15 Cold Heading Steel

余刚; 袁武华; 刘泽亚; 傅强

您当前的位置：

首页 >

文章列表页 >

Hot Ductility of Continuous Casting Billet of 10B15 Cold Heading Steel

更新时间：2026-01-21

- Hot Ductility of Continuous Casting Billet of 10B15 Cold Heading Steel
- Special Steel Vol. 32, Issue 2, Pages: 63-65(2011)
- 作者机构：
  
  1. 湖南华菱湘潭钢铁有限公司,湘潭,411101
  2. 湖南大学材料科学与工程学院,长沙,410082
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：01 November 2010，
  
  Online First：10 November 2022，
  
  Published：10 November 2011
- 稿件说明：
移动端阅览
余刚, 袁武华, 刘泽亚, et al. Hot Ductility of Continuous Casting Billet of 10B15 Cold Heading Steel[J]. Special Steel, 2011, 32(2): 63-65.
DOI：

余刚, 袁武华, 刘泽亚, et al. Hot Ductility of Continuous Casting Billet of 10B15 Cold Heading Steel[J]. Special Steel, 2011, 32(2): 63-65. DOI：

摘要

通过Gleeble-1500热模拟机研究了10B15冷镦钢(%:0.17C、0.16Si、0.46Mn、0.017P、0.025S、0.0002Ti、0.000 8Als、0.001 4B)150 mm×150 mm连铸坯应变速率0.0005～0.001s-1在700～1 000℃的热塑性。结果表明

10B15冷镦钢连铸坯在850～900℃有高温脆性;应变速率的降低促进动态再结晶的发生

可以提高高温塑性;细小的B、Ti和Al的氮化物在晶界的析出起晶界钉扎作用

阻碍了晶界的滑移和动态再结晶的发生

从而使钢的高温塑性降低。

Abstract

The hot ductility of 150 mm x 150 mm casting billet of 10B15 cold heading steel (% ： 0. 17C

0. 16Si

0. 46Mn

0. 017P

0. 025S

0.000 2Ti

0.000 8A1

0.001 4B) with strain rate 0.000 5 -0. 001 s

-1

at 700 1 000 ℃ has been studied by using Gleeble-1500 thermal simulator. Results show that the casting billet of 10B15 cold heading steel has hot brittleness at 850 ~ 900 °C ； the dynamic recrystallization is promoted by decreasing strain rate led to increase of hot ductility ； the nitrides of B

Ti and Al precipitate at grain boundary to take pin pinning effect on grain boundary to hinder slide of boundary and occurrence of dynamic recrystallization led to decrease of the hot ductility of steel.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Model of Dynamic Recrystallization Critical Strain in Ferrite Deformation of Ti-IF Steel

Modelling of Dynamic Recrystallization for a Ti-IF Steel

Finite Element Simulation for Effect of Initial Rolling Temperature on Change of Rolling Dynamic Structure of Steel 42CrMo4

Effect of RE on Hot Plasticity of V Microalloying Heavy Rail Steel

A Study on Dynamic Recrystallization of Austenite Stainless Steel 321

Related Author

徐楚韶

赵嘉蓉

刘显军

熊俊伟

徐光

徐楚韶

安胜利

Related Institution

重庆大学材料科学与工程学院

北京科技大学冶金与生态工程学院

包头钢铁职业技术学院

包钢(集团)公司

技术中心

⁰