Effect of Mn on Physical Properties of Concasting Bloom of Medium Carbon Steel at High Temperature

更新时间：2026-01-21

- Effect of Mn on Physical Properties of Concasting Bloom of Medium Carbon Steel at High Temperature
- Special Steel Vol. 32, Issue 4, Pages: 64-66(2011)
- 作者机构：
  
  包钢(集团)公司技术中心,包头,014010
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：20 February 2011，
  
  Online First：03 November 2022，
  
  Published：03 November 2011
- 稿件说明：
移动端阅览
刘平, 姜丽, 李峰. Effect of Mn on Physical Properties of Concasting Bloom of Medium Carbon Steel at High Temperature[J]. Special Steel, 2011, 32(4): 64-66.
DOI：

刘平, 姜丽, 李峰. Effect of Mn on Physical Properties of Concasting Bloom of Medium Carbon Steel at High Temperature[J]. Special Steel, 2011, 32(4): 64-66. DOI：

摘要

120 t转炉-LF-VD-连铸工艺生产37Mn5钢的280 mm×380 mm连铸坯易出现纵向裂纹。用Gleeble1500D热模拟试验机试验和分析了在1300～800℃时37Mn5钢(%:0.34～0.38C、1.30～1.55Mn)和45钢(%:0.42～0.50C、0.50～0.80Mn)280 mm×380 mm连铸坯的热塑性和力学性能

以及室温和1300℃之间加热和冷却时的膨胀-收缩效应。与45钢比较

得出≤950℃时37Mn5钢连铸坯的热塑性较低

在相变范围的体积变化较45钢铸坯大

导致37Mn5钢铸坯出现纵向裂纹。因此应降低37Mn5钢铸坯在540～870℃范围内的加热和冷却速度

以避免产生纵向裂纹。

Abstract

The longitudinal crack of 37Mn5 steel 280 mm x 380 mm concasting bloom produced by 120 t converter- LF-VD-bloom caster process often occurs in production. The hot plasticity and mechanical properties of 280 mm x 380 mm concasting bloom of 37Mn5 steel (% ； 0. 34 ~ 0. 38C t 1. 30 - 1. 55Mn) and 0. 45C steel (%: 0. 42 〜0. 50C

0. 50 〜 0. 80Mn) at 1 300 - 800 ℃ and their dilatometric-shrinking effect during heating and cooling between ambient and 1 300 °C have been tested and analyzed by using Gleeble 1500D thermal simulation machine. It is obtained that as compared with 0. 45C steel bloom

at W950 °C the hot plasticity of 37Mn5 steel bloom is lower and the change of volume at phase transformation range is larger than that of 0. 45C steel bloom led to occurrence of longitudinal crack. Therefore

heating and cooling speed of 37Mn5 steel bloom between 870 Y and 540 Y should be slowed down to avoid occurrence of longitudinal crack.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

A Study on High Temperature Mechanical Properties of GCr15 Bearing Steel

An Analysis on Forming Mechanism of Longitudinal Crack of N08810 Corrosion Resistant Alloy 200 mm Thickness Casting Slab

Effect of C, Mn, Cr on Hardenability of Medium Carbon MnB Steel 228 Pitch Crawler Belt

Simulation Calculation on 250 ~ 320 mm Casting Slab during Stacking Slow Cooling Process

Effect of Carbon and Boron Content on Mechanical Properties of Casting Bloom of Low Carbon Cold Heading Steel at Elevated Temperature

Related Author

路文刚

朱立光

马骏

郑宏光

黄坚

郭亮亮

马天军

邓通武

Related Institution

河北理工大学冶金与能源学院

上海交通大学材料科学与工程学院

宝山钢铁股份有限公司研究院

攀钢集团研究院有限公司

首钢技术研究院

⁰