Effect of Forming Pressure on Microstructure and Magnetic Properties of Sintered Nd-Fe-B Magnet

张晓鹏; 于旭光

您当前的位置：

首页 >

文章列表页 >

Effect of Forming Pressure on Microstructure and Magnetic Properties of Sintered Nd-Fe-B Magnet

更新时间：2026-01-21

- Effect of Forming Pressure on Microstructure and Magnetic Properties of Sintered Nd-Fe-B Magnet
- Special Steel Vol. 33, Issue 2, Pages: 46-48(2012)
- 作者机构：
  
  石家庄铁道大学材料学院,石家庄,050043
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：19 September 2011，
  
  Online First：18 October 2022，
  
  Published：18 October 2012
- 稿件说明：
移动端阅览
张晓鹏, 于旭光. Effect of Forming Pressure on Microstructure and Magnetic Properties of Sintered Nd-Fe-B Magnet[J]. Special Steel, 2012, 33(2): 46-48.
DOI：

张晓鹏, 于旭光. Effect of Forming Pressure on Microstructure and Magnetic Properties of Sintered Nd-Fe-B Magnet[J]. Special Steel, 2012, 33(2): 46-48. DOI：

摘要

在于法制备烧结钕铁硼生产线上

研究了11.54 MPa和9.23 MPa两种成形压力对Φ9.5mm烧结钕铁硼磁体(/%:31.00Pr+Nd、1.20B、0.20Al、余Fe)微观组织与磁性能的影响。结果表明

成形压力增大可以改善晶粒分布的不均匀性

提高取向度

从而提高剩磁与磁能积;但成形压力增大易使晶粒尺寸增大

从而使矫顽力降低。

Abstract

The effect of two kinds of forming pressure- 11.54 MPa and 9.23 MPa on microstructure and magnetic properties of Nd-Fe-B magnet has been studied at production line for Φ9. 5 mm sintered Nd-Fe-B magnet (/% ： 31.00Pr + Nd

1.20B

0.20Al

remainder Fe) manufactured by dry process. Results show that with increasing forming pressure the unevenness of grain size distribution is improved and the grain orientation increases in order to increase remained magnetic induction intensity and magnetic energy product of sintered magnet ； but with increasing forming pressure the grain size increases in order to decrease the intrinsic coercive force of magnet.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Forging Process on Microstructure and Properties of Fe10Cr10Co Soft Magnetic Alloy

Effect of Solution Temperature on Microstructural Evolution and Tensile Properties of Hot-rolled Haynes 230 Alloy Bar

Effect of Progressive Solid Solution Treatment on the Structure and Properties of 316H Stainless Steel

Effect of Quenching Temperature on Mechanical Properties of M₆C Reinforced 2 200 MPa Ultra-high Strength Steel

Influence of Microstructure on DWTT Performance of Thin-wall X65M Pipeline Steel

Related Author

Han Zhongjian

Li Zhu

Ma Jing

Wang Yanmou

Liu Jie

Wei Hang

Xu Xiaoyi

Guo Liang

Related Institution

Xi'an Gangyan Special Alloy Co.，Ltd

Wuxi Paike New Materials Technology Co.， Ltd.

Metallurgical College， Northeastern University

Chongqing Materials Research Institute Co.， Ltd.

Chongqing Institute of Instrument Materials

⁰