Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting

李熠; 倪红卫; 张华; 罗荣华

您当前的位置：

首页 >

文章列表页 >

Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting

更新时间：2026-01-21

- Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting
- Special Steel Vol. 33, Issue 2, Pages: 10-13(2012)
- 作者机构：
  
  武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：11 October 2011，
  
  Online First：13 October 2022，
  
  Published：13 October 2012
- 稿件说明：
移动端阅览
李熠, 倪红卫, 张华, et al. Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting[J]. Special Steel, 2012, 33(2): 10-13.
DOI：

李熠, 倪红卫, 张华, et al. Numerical Simulation of Mold Electromagnetic Stirring for 380 mm x 280 mm Bloom Casting[J]. Special Steel, 2012, 33(2): 10-13. DOI：

摘要

利用有限元分析软件

建立了380 mm×280 mm大方坯结晶器电磁搅拌的三维数学模型

系统研究了电磁搅拌工艺参数(电流250～500 A

频率1.5～3.0 Hz

结晶器铜板厚度34～40 mm)对结晶器内电磁场的分布影响。结果表明

结晶器内磁感应强度沿铸流轴向呈"两端小、中间大"分布;电流从350 A增大到500 A

搅拌器中心的磁感应强度呈线性递增;频率由1.5Hz增大到3.0Hz

搅拌器中心磁感应强度仅减小0.0015 T;随着结晶器铜板厚度的增大

铸坯宽面、窄面和角部的磁感应强度都减小。在实际连铸U71Mn重轨钢中

电流应该维持在400 A以上。

Abstract

A three-dimensional math model of electromagnetic stirring of mold for 380 mm x 280 mm bloom casting is established by using finite element analytic software and the effect of electromagnetic stirring parameters (current intensity 200-500 A

frequency 1.5-3.0 Hz

thickness of mold copper plate 34-40 mm) on distribution of magnetic field in mold is systematically studied. Results show that the max magnetic induction intensity is at center of axis direction of strand and the lower values of magnetic induction intensity are at top and bottom of mold ； with increasing current intensity from 350 A to 500 A

the magnetic induction intensity at center of stirrer increases linearly ； with increasing current frequency from 1.5 Hz to 3.0 Hz

the magnetic induction intensity at center of strand decreases only by 0.0015 T； and with increasing thickness of mold copper plate

the magnetic induction intensity at wide surface

narrow surface and comer of the strand all decreases. In actual casting heavy rail steel U71Mn process

current intensity should be more than 400 A.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Numerical Simulation on Optimization of Inclination of Submerged Nozzle for 220mm x 1600mm Slab Casting and Application

Numerical Simulation of 80 mm Extra-thick Plate Stacking Slow Cooling for EH420 Marine Steel

Numerical Simulation of Solidification Structure for 4J36 Invar Alloy Ingot

Production Process Practice of 42CrMoM Steel for 12.9 Grade High Strength Wind Power Fasteners

Numerical Simulation of Flow and Solidification Behavior of Medium Mn steel in Thin Slab Mold

Related Author

宁林新

解家英

刘金刚

张利君

Jiang Dongbin

Liu Zhaoxia

Liu Jun

Sun Xianjin

Related Institution

首钢技术研究院

绿色可循环钢铁流程北京市重点实验室

User Application Technology Research Institute， Citic Pacific Special Special Steel Group Co.，Ltd.， Jiangyin

School of Metallurgical and Ecological Engineering，University of Science and Technology Beijing

Jiangyin Xingcheng Special Steel Works Co.， Ltd.， Jiangyin

⁰