Evaluation Method and Effective Factor on Intergranular Corrosion Susceptibility of 430 Ferrite Stainless Steel

更新时间：2026-01-21

- Evaluation Method and Effective Factor on Intergranular Corrosion Susceptibility of 430 Ferrite Stainless Steel
- Special Steel Vol. 33, Issue 5, Pages: 57-60(2012)
- 作者机构：
  
  1. 昆明理工大学材料科学与工程学院,昆明,650093
  2. 钢铁研究总院结构材料研究所,北京,100081
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：21 March 2012，
  
  Online First：10 October 2022，
  
  Published：10 October 2012
- 稿件说明：
移动端阅览
邵泽斌, 陈海涛, 郎宇平, et al. Evaluation Method and Effective Factor on Intergranular Corrosion Susceptibility of 430 Ferrite Stainless Steel[J]. Special Steel, 2012, 33(5): 57-60.
DOI：

邵泽斌, 陈海涛, 郎宇平, et al. Evaluation Method and Effective Factor on Intergranular Corrosion Susceptibility of 430 Ferrite Stainless Steel[J]. Special Steel, 2012, 33(5): 57-60. DOI：

摘要

采用双环-电化学(DL-EPR)法评价了热轧和退火430铁素体不锈钢(/%:0.038C、16.83Cr)的晶间腐蚀敏感性。确定了一种适合的试验参数

试验溶液为0.05 mol/L H

+0.001 mol/L KSCN+0.01 mol/LNa

扫描速率为正扫5.0 mV/s

反扫1.67 mV/s

当Ra值(反扫电流Ir/正扫电流Ia)越高

晶间腐蚀敏感性越严重。试验结果表明

热轧后的430铁素体不锈钢存在明显的晶间腐蚀敏感性

空冷试样的舶值比水冷的高;经过750～850℃10 min退火处理能够有效减轻和消除热轧430铁素体不锈钢晶间腐蚀敏感性。

Abstract

A double loop-electrochemical proteinomimetic reactivation (DL-EPR) method is used to evaluate the intergranular corrosion (IGC) susceptibility of hot rolled and annealed 430 ferrite stainless steel (0. 038% C

16. 83% Cr). A suitable test parameter- in test solution 0. 05 mol/L H

+0. 001 mol/L KSCN + 0. 10 mol/L Na

with anodic potential scanning rate 5. 0 mV/s and reverse potential scanning rate 1.67 mV7s is determined

and the larger the value Ra (reverse scanning current Ir / anodic scanning current la) the - more serious the intergranular corrosion susceptibility of steel. Test results show that the hot rolled 430 ferritic stainless steel has obvious intergranular corrosion susceptibility and the Ra value of the sample air-cooled after rolling is larger than that

of the sample water-cooled after rolling； with annealed treatment at 750 〜850℃ for 10 min the intergranular corrosion susceptibility of hot rolled 430 ferrite stainless steel is effectively reduced and eliminated.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Basicity of Tundish Covering Flux on Metallurgy Quality of Ferrite Stainless Steel

Effect of Nitrogen on Mechanical Properties and Corrosion Resistance of Austenite Stainless Steel 316LN

Related Author

王伟

张润平

任国

杨瑞军

白晋钢

陈海涛

罗毅军

Related Institution

钢铁研究总院特殊钢研究所

中国核动力研究设计院设计所

⁰