Evolution of Structure and Texture in 3 % Si Steel during Hot and Cold Rolling Process based on CSP Technology

闫志飞; 金自力; 计云萍; 刘朋成; 张利博

您当前的位置：

首页 >

文章列表页 >

Evolution of Structure and Texture in 3 % Si Steel during Hot and Cold Rolling Process based on CSP Technology

更新时间：2026-01-21

- Evolution of Structure and Texture in 3 % Si Steel during Hot and Cold Rolling Process based on CSP Technology
- Special Steel Vol. 33, Issue 2, Pages: 65-67(2012)
- 作者机构：
  
  内蒙古科技大学材料与冶金学院,包头,014010
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：20 October 2011，
  
  Online First：20 October 2022，
  
  Published：20 October 2012
- 稿件说明：
移动端阅览
闫志飞, 金自力, 计云萍, et al. Evolution of Structure and Texture in 3 % Si Steel during Hot and Cold Rolling Process based on CSP Technology[J]. Special Steel, 2012, 33(2): 65-67.
DOI：

闫志飞, 金自力, 计云萍, et al. Evolution of Structure and Texture in 3 % Si Steel during Hot and Cold Rolling Process based on CSP Technology[J]. Special Steel, 2012, 33(2): 65-67. DOI：

摘要

3%Si钢(/%:0.067C、3.09Si、0.34Mn、0.007P、0.003S、0.70Cu、≤0.005Al、0.0080～0.0120N)由50kg真空感应炉冶炼

并在实验室轧机经6道次热轧成3.5mm板

终轧温度850℃

卷取温度650℃

热轧板经常化处理后由4辊可逆轧机6道次冷轧成0.50mm薄板。分析结果表明

热轧板表面主要为随机分布较大的等轴晶

中心处由细小等轴晶和长条状晶粒组成

并出现了很强的旋转立方织构{001}〈110〉。经过冷轧

薄板表面出现了很强的α织构和γ织构组分

并且冷轧板保留了热轧的{001}〈110〉旋转立方织构。

Abstract

The 3% Si steel (/% : 0.067C

3.09Si

0.34Mn

0.007P

0.003S

0.70Cu

≤0.005Al

0.0080-0.0120N) is melted by a 50 kg vacuum induction furnace and hot rolled to 3.5mm plate by 6 pass with finishing rolling at 850 Y and coiling at 650 °C by laboratory mill

then normalized hot rolled plate is cold rolled to 0.5 mm sheet by 4 roll reversing mill with 6 passes. Analysis results show that at surface region of hot rolled plate there are mainly random distributed larger equiaxial grains

the center area consists of fine equiaxial grains and lath shape grains and the strong rotating cube texture {001}〈110〉components occur in center area； After cold rolling

the strong a and y textures occur at surface region and the hot rolled {001}〈110〉rotating cube textures are retained in cold rolled sheet.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Structure and Texture of CSP Cold-Rolled Sheet of Low Carbon Steel DC03

Hot Rolling and Properties of 304/440/304 Stainless Steels Clad Plate for Knife Products

Influence of Cold Reduction on Structure and Properties of DQ Level Deep-Drawing Strip Steel

Effect of Rolling Process on Structure, Texture and Properties of X80 Pipeline Steel

Effect of Cooling Rate on Structure of Hot Rolled Round Bar of Steel 40CrMo

Related Author

罗年高

余驰斌

张云祥

杨海林

成小军

伍康勉

刘靖

李亮

Related Institution

武汉科技大学材料与冶金学院

湖南涟源钢铁集团公司

北京科技大学材料科学与工程学院

包头钢铁集团公司薄板厂

首钢技术研究院

⁰