Effect of Pearlite Segregation Band and Ti( C,N) on Layering of Tensile Fracture of Steel HG70C Hot Rolled Plate

王芹; 彭其春; 王理猷; 陈凯; 李具中; 李伟

您当前的位置：

首页 >

文章列表页 >

Effect of Pearlite Segregation Band and Ti( C,N) on Layering of Tensile Fracture of Steel HG70C Hot Rolled Plate

更新时间：2026-01-21

- Effect of Pearlite Segregation Band and Ti( C,N) on Layering of Tensile Fracture of Steel HG70C Hot Rolled Plate
- Special Steel Vol. 33, Issue 5, Pages: 65-68(2012)
- 作者机构：
  
  1. 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
  2. 武汉钢铁(集团)公司,武汉,430080
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：30 March 2012，
  
  Online First：10 October 2022，
  
  Published：10 October 2012
- 稿件说明：
移动端阅览
王芹, 彭其春, 王理猷, et al. Effect of Pearlite Segregation Band and Ti( C,N) on Layering of Tensile Fracture of Steel HG70C Hot Rolled Plate[J]. Special Steel, 2012, 33(5): 65-68.
DOI：

王芹, 彭其春, 王理猷, et al. Effect of Pearlite Segregation Band and Ti( C,N) on Layering of Tensile Fracture of Steel HG70C Hot Rolled Plate[J]. Special Steel, 2012, 33(5): 65-68. DOI：

摘要

针对低合金高强焊接钢HG70C(/%:0.069～0.077C、0.07～0.11Si、1.79～1.83Mn、0.011～0.012P、0.004～0.005S、0.121～0.123Ti、0.046～0.047Nb)8～12 mm板拉伸试验后试样断口出现分层的现象

利用金相显微镜、扫描电镜和能谱仪对断口形貌及分层附近区域进行了观察和分析

并且统计分析了实际生产中加热参数。结果表明

该钢种分层与热轧工艺无关

主要与中心珠光体偏析带及偏析处大颗粒Ti的碳氮化物有关

并且在铸坯中发现已有2μm左右的该类析出物颗粒存在

它们成为疲劳源导致拉伸断口分层。

Abstract

According to the phenomena of 8 ~ 12 mm plate tensile fracture layering of low alloy high strength welded steel HG70C (/%: 0. 069 ~D. 077C

0. 07 〜0. HSi

1. 79 〜L83Mn

0.011 〜0.012P

0. 004 ~ 0. 005S

0. 121 〜 0. 123Ti

0. 046 - 0. 047 Nb)

the morphology of fracture and area near layering are observed and analyzed by using optical and scanning electron microscope and energy spectrum analyser

and the statistical analysis of heating process parameters of bloom in real production is carried out. Results show that the layering of the steel plate tensile fracture has nothing to do with heating process for hot rolling

it is mainly related to center pearlite segregation band and large titanium carbo-nitride

and this precipitates with 2μm is found in casting bloom which are fatigue source lad to layering of tensile fracture.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Application of Carbo-nitride Precipitation Model in Concasting Process of Nb-Bearing Microalloyed Steel for Ship Plate

Development and Experimentation on a New Partitioning Agent of Desulphurization Slag in Hot Metal Blowing Process

Study on Microstructure and Properties of High Nitrogen Stainless Bearing Steel

Related Author

张小欢

刘珂

李阳

张家泉

刘学华

张乔英

张建平

刘勇

Related Institution

北京科技大学钢铁冶金系与循环冶金教育部重点实验室

马鞍山钢铁股份有限公司

新疆八一钢铁集团股份有限公司第二炼钢厂

钢铁研究总院特殊钢研究所 2. 钢铁研究总院中心实验室

⁰