Study and Analysis on Thermodynamics of TiN (C) Precipitating Behavior in Bearing Steel GCrl5

赵东伟; 包燕平; 王敏; 马文俊; 苏利川

您当前的位置：

首页 >

文章列表页 >

Study and Analysis on Thermodynamics of TiN (C) Precipitating Behavior in Bearing Steel GCrl5

更新时间：2026-01-21

- Study and Analysis on Thermodynamics of TiN (C) Precipitating Behavior in Bearing Steel GCrl5
- Special Steel Vol. 33, Issue 5, Pages: 7-11(2012)
- 作者机构：
  
  1. 北京科技大学1钢铁冶金新技术国家重点实验室
  2. 冶金与生态工程学院,北京,100083
  3. 杭州钢铁集团公司,杭州,310022
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：09 October 2022，
  
  Published：09 October 2012
- 稿件说明：
移动端阅览
赵东伟, 包燕平, 王敏, et al. Study and Analysis on Thermodynamics of TiN (C) Precipitating Behavior in Bearing Steel GCrl5[J]. Special Steel, 2012, 33(5): 7-11.
DOI：

赵东伟, 包燕平, 王敏, et al. Study and Analysis on Thermodynamics of TiN (C) Precipitating Behavior in Bearing Steel GCrl5[J]. Special Steel, 2012, 33(5): 7-11. DOI：

摘要

通过对TiN(C)生成热力学和动力学计算

分析研究了GCr15轴承钢(0.97%C、1.45%Cr)凝固过程中TiN(C)夹杂的析出规律以及夹杂物长大的影响因素。研究表明

液相线温度以上

TiN不会析出

只有在液相线至固相线温度之间

当凝固百分数fs≥0.4～0.5

1694～1703 K时TiN析出;整个凝固过程中

TiC在凝固末端有少量析出

当fs≥0.87～0.92

1633～1643 K时

降低Ti、N含量能够显著降低TiN的析出温度和尺寸。冷却速率不会影响TiN的析出温度

但对夹杂长大也有较为明显的影响。控制析出TiN夹杂的条件为:Ti]/%≤0.006、[N]/%≤0.004和较大冷却速率。

Abstract

According to the thermodynamic and kinetic calculation of TiN (C)

the precipitation rule of TiN (C) inclusions in solidifying process of bearing steel GCrl5 (0. 97% C

1.45% Cr) and the influence factors of inclusion growing are analyzed and studied. Study results show that above liquidus there is no precipitate of TiN

only between liquidus and solid phase curve i. e. as solidification percentage fs ≥ 0.4 -0. 5 at 1 694 〜1 703 K the TiN precipitates

and during whole solidifying process there is minor TiC precipitating at solidified front

as fs ≥ 0. 87 - 0. 92 at 1 633 ~ 1 643 K

with decreasing Ti and N content in steel the precipitated temperature and size of TiN obviously decrease. The cooling rate has not influence on precipitated temperature of TiN but has more obvious influence on inclusion growing. The conditions to control TiN inclusion precipitation are [Ti]/% ≤ 0. 006

[N]/% ≤ 0.004 and larger cooling rate.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Key Metallurgical Technologies for Smelting 1Cr13 Stainless Steel via ANS-OB Process

Effect of Refining Slag Basicity on the Molten Steel Cleanliness of GCr15SiMn Bearing Steel

Characteristics and Evolution of Non-metallic Inclusions in Metallurgical Production of GCr15 Bearing Steel

The Metallurgical Mechanisms of Inclusions in the FGH4096 Alloy during Electron Beam Refining

Process Analysis and Experiment of Precise Control of Nitrogen Content in Pressure Smelting of Mn18Cr18N

Related Author

Lu Zhihao

Teng Xingze

Xu Mengchun

Jin Zhe

Fu Xianbin

Li Boyang

Guo Yunfei

Qiu Mian

Related Institution

Iron & Steel Research Institute of Ansteel Group

State Key Laboratory of Metallic Materials for Marine Equipment and Applications

State Key Laboratory of Advanced Metallurgy， University of Science and Technology Beijing

Shanxi Taizhong Intelligent Equipment Co.， Ltd.

State Key Laboratory of Intelligent Mining Equipment Technology

⁰