- Analysis on Unqualified Pressure Vessel Steel Plate by Nondestructive Test and Optimization of Process
- Special Steel Vol. 38, Issue 5, Pages: 17-21(2017)
- 作者机构：
  
  1. 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
  2. 武汉钢铁股份有限公司炼钢总厂,武汉,430083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：25 April 2017，
  
  Online First：11 July 2022，
  
  Published：11 July 2017
- 稿件说明：
移动端阅览
林强, 张华, 陈国威, et al. Analysis on Unqualified Pressure Vessel Steel Plate by Nondestructive Test and Optimization of Process[J]. Special Steel, 2017, 38(5): 17-21.
DOI：

林强, 张华, 陈国威, et al. Analysis on Unqualified Pressure Vessel Steel Plate by Nondestructive Test and Optimization of Process[J]. Special Steel, 2017, 38(5): 17-21. DOI：

摘要

试验12MnNiVR压力容器钢板（/%:≤0.15C，0.15~0.40Si，1.20~1.60Mo，≤0.008P，≤0.018S，0.15~0.40Ni，≤0.30Cu，0.02~0.06V）的生产工艺为KR铁水脱硫-90t BOF-RH-210~300mm板坯连铸-轧制成20~30mm钢板，用扫描电镜分析了容器钢板，研究12MnNiVR容器钢RH精炼和连铸过程钢液全氧含量、夹杂物数量、粒径分布、形貌和组成。结果表明，Al

夹杂物经轧制发展形成线状缺陷是钢板探伤不合格主要原因；RH精炼过程钢水偏低，吹氧量高和连铸过程钢液二次氧化易造成Al

夹杂物超标；通过控制BOF出钢温度1650℃

RH前钢水温度≥1610℃，减少RH精炼过程升温吹氧量，RH循环时间≥10min，加强保护浇铸等工艺措施，容器钢板探伤合格率由96.85%提高到99.07%。

Abstract

The production process of tested 12MnNiVR pressure vessel steel plate (/% : ≤0.15C

0.15~0.40Si

1.20~1.60Mn

≤0.008P

≤0.018S

0.15~0.40Ni

≤0.30Cu

0.02~0.06V) is KR metal desulphurization- 90t BOF- RH- 210~300mm slab casting-rolling to 20~30mm steel plate. The liquid total oxygen content

inclusions number

inclusion size distribution

morphology and ingredient of unqualified specimen of 12MnNiVR pressure vessel steel plate in RH refining and casting process have been studied by scanning electron microscope. Results show that the linear Al

defect formed by rolling is main reason of un-qualification of plate by nondestructive test; with process measures including controlling BOF tapping temperature 1650℃

liqui

d temperature before RH refining ≥l610℃

decreasing oxygen blowing amount in RH refining process

strengthening shielding process and RH cycling time ≥10min

the qualified rate of pressure vessel steel plate by nondestructive test increases from original 96.85% to 99.07%.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Industrial Experimental Study on Removal of Inclusions in Steel by Nitrogen Addition and Release Method

Influence of Nozzles Blocking of RH Up-Snorkel on Circulation Flow Rate

A Study of Water Modeling on Circulation Flow Rate in RH Vacuum Refining Process

Process Practice of Control Oxygen Content in Bearing Steel GCr15 Produce by 80t BOF-LF-VD-CC Flowsheet

Related Author

Liu Jianhua

He Yang

Li Wei

Lin Junyu

Chen Xiujun

Bi Sheng

Zhang Yudi

吴华杰

Related Institution

Institute of Engineering Technology University of Science and Technology Beijing

Dongbei Special Steel Group Trade Co.， Ltd.

北京科技大学冶金与生态工程学院

北京科技大学冶金工程研究院

辽宁科技大学材料与冶金学院

⁰