- Numerical Simulation of Heat Transfer and Solidification of Liquid at Action of Flow Field in Mold for Slab
- 特殊钢 2010年31卷第6期页码：4-6
- 作者机构：
  
  1. 辽宁科技大学材料与冶金学院,鞍山,114051
  2. 鞍钢集团朝阳鞍凌钢铁有限公司,朝阳,122000
- 作者简介：
  
  [ "许长军(1981-),男，博士研究生，炼钢、连铸工艺研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2010-02-01，
  
  网络首发：2022-10-27，
  
  纸质出版：2010-10-27
- 稿件说明：
移动端阅览
许长军, 汪琦, 胡林, 等. 板坯结晶器内流场作用下钢液传热凝固的数值模拟[J]. 特殊钢, 2010,31(6):4-6.

许长军, 汪琦, 胡林, et al. Numerical Simulation of Heat Transfer and Solidification of Liquid at Action of Flow Field in Mold for Slab[J]. Special Steel, 2010, 31(6): 4-6.
许长军, 汪琦, 胡林, 等. 板坯结晶器内流场作用下钢液传热凝固的数值模拟[J]. 特殊钢, 2010,31(6):4-6. DOI：

许长军, 汪琦, 胡林, et al. Numerical Simulation of Heat Transfer and Solidification of Liquid at Action of Flow Field in Mold for Slab[J]. Special Steel, 2010, 31(6): 4-6. DOI：

摘要

以钢厂230 mm×2 150 mm板坯连铸机为研究对象

通过三维数值模拟分析了拉坯速度(0.8～2.3m/min)、水口浸入深度(100～200 mm)、铸坯宽度(1 100～2 150 mm)对结晶器内流场作用下的钢液传热、凝固特征的影响。结果表明

拉坯速度等参数变化不会改变结晶器内钢液流动的基本特征

但会显著影响到结晶器内窄边坯壳的发育状况。水口浸深、铸坯宽度和拉坯速度的变化对于结晶器熔池液面钢水过热度也有不同程度影响:小断面

大拉速和水口浸入深度较小时熔池液面过热度较大

最大达6.2 K。

Abstract

With a 230 mm x2 150 mm slab caster at steelmaking works as an object of study

the effect of cast speed (0. 8 ~2. 3 m/min)

immersion depth of submerged nozzle (100 -200 mm) and slab width (1 100 ~2 150 mm) on heat transfer and solidification of liquid at action of flow field in mold has been analyzed by 3 dimensional numerical simulation. Results show that the change of casting speed and other parameters has no influence on basic characteristics of liquid flowing in mold

but can effect the development of slab shell at narrow side in mold. The change of immersion depth of submerged nozzle

slab width and casting speed effects overheat extent of liquid on surface of bath in mold in varying degrees

i. e. with smaller cross section

larger casting speed and smaller immersion depth of submerged nozzle

the overheat extent of liquid on surface of bath is larger

maximum value is up to 6. 2 K.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

板坯连铸结晶器钢液流场的数值模拟和优化

电磁搅拌对电渣重熔钢锭温度场的影响

420 mm x 1100 mm板坯连铸结晶器吹氩对流场和温度场影响的数值模拟

多孔水口对轴承钢280 mm x325 mm铸坯结晶器钢液流场和温度场的影响

304不锈钢棒线材热连轧温度场的数值模拟