- 轧后冷却工艺对模拟CSP含铜Hi-B钢热轧组织和结构的影响
- Effect of Cooling Process after Rolling on Structure and Texture of Simulated CSP Hot-Rolled Hi-B Steel Bearing Copper
- 特殊钢 2018年39卷第2期页码：56-59
- 作者机构：
  
  1. 武汉工程大学邮电与信息工程学院,武汉,430073
  2. 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
- 作者简介：
  
  [ "余冲(1987-),女，硕士,2010年武汉科技大学(本科)毕业，金属压力加工组织与性能研究。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2017-10-10，
  
  网络首发：2022-07-04，
  
  纸质出版：2018-07-04
- 稿件说明：
移动端阅览
余冲, 肖欢. 轧后冷却工艺对模拟CSP含铜Hi-B钢热轧组织和结构的影响[J]. 特殊钢, 2018,39(2):56-59.

余冲, 肖欢. Effect of Cooling Process after Rolling on Structure and Texture of Simulated CSP Hot-Rolled Hi-B Steel Bearing Copper[J]. Special Steel, 2018, 39(2): 56-59.
余冲, 肖欢. 轧后冷却工艺对模拟CSP含铜Hi-B钢热轧组织和结构的影响[J]. 特殊钢, 2018,39(2):56-59. DOI：

余冲, 肖欢. Effect of Cooling Process after Rolling on Structure and Texture of Simulated CSP Hot-Rolled Hi-B Steel Bearing Copper[J]. Special Steel, 2018, 39(2): 56-59. DOI：

摘要

以模拟CSP工艺-真空感应炉熔炼含铜Hi-B钢(/%:0.06C

3.38Si

0.14Mn

0.013P

0.003S

0.019Als

0.37Cu

0.0015O

0.0087N)模铸成210mm×120mm×60mm板

Φ350mm二辊热轧机1065℃开轧经5道次从60mm轧成3.5mm板(终轧865℃)为试验基板

研究了轧后水冷和轧后水冷至580℃再空冷两种冷却工艺对实验钢组织和织构的影响。结果表明

热轧后水冷到580℃再空冷到室温的冷却方式有助于获得更高取向精准度的高斯织构、更低比例的黄铜织构以及其他合理的织构组成

较轧后水冷工艺更加适合实验钢。

Abstract

The simulated CSP process of tested plate of Hi-B steel bearing copper (/%: 0.06C

3.38Si

0.14Mn

0.013P

0.003S

0.019Als

0.37Cu

0.0015O

0.0087N) is melting by vacuum induction furnace and mold casting to 210mmx120mmx60mm plate

rolling at 1065℃ from 60mm to 3.5mm plate with finishing rolling at 865°C by Φ350mm two-high hot rolling mill and 5 passes. The effect of both processes-water cooling after rolling and water cooling to 580℃

air cooling after rolling on structure and texture of tested steel has been studied. Results show that the cooling process of water cooling to 580°C

air cooling to room temperature after hot-rolling is available to get Goss texture with higher orientation accuracy and lower content of Brass texture

and other reasonable texture component

as compared with water cooling process after rolling it is more suitable for tested steel.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

稀土对冷轧无取向电工钢成品组织和磁性能的影响

初次再结晶退火工艺对3%Si取向硅钢组织和织构的影响

连续退火温度对390 MPa级IF钢组织、织构和力学性能的影响

热轧板常化工艺对取向硅钢冷轧板退火组织和性能的影响

初次再结晶退火对模拟CSP含Cu Hi-B硅钢组织和织构的影响