Abstract: The  structure  evolution  of a  Nb-microalloyed  extra-low  carbon  steel  0.03C- 1.05Mn-0.6Cr-0.08Nb  during 1200  ℃  heating,then  cooling  to  850  ℃  and  reducing  50%,holding  at  850  ℃  for  20~1000  s  fast  cooling  to  450  ℃,air  cooling has been simulated and tested by Thermecmastor -Z thermal simulator. The test results showed that with increasing  holding time after reduction  50%,the amount of acicular ferrite and bainite in  steel and the dislocation density in  structure  decreased,where  the  size  of  martensite-austerite(M-A)island  increased;  As  the  holding  time  after  reduction  50%  was  more  than  50  s,  the  micro  hardness(Hv10)value  quick  decreased  but  that  more  than  500  s  the  Hv10  hardness  value  decreased  slowly.

Key words: Extra-Low Carbon,Nb Micro-Alloying,Thermomechanical Control Process,Thermal Simulation, Structure Evolution

摘要： 用Thermecmastor-Z型热模拟机模拟试验了成分(%)为:0.03C-1.05Mn-0.6Cr-0.08Nb的Nb超低碳钢加热1 200℃后冷至850℃压缩变形50%,并在850℃下保温20~1 000 s后快冷至450℃,再空冷的过程中的组织演变。试验结果表明,随50%变形后保温时间的延长,钢中针状铁素体及贝氏体数量减少,多边铁素体数量增加,马氏体-奥氏体(M-A)岛尺寸增大,组织中位错密度降低;当50%变形后,保温时间>50 s时,显微硬度(Hv10)值快速下降,保温时间≥500 s时,Hv10值下降较慢。

关键词: 超低碳, Nb微合金化, 控轧控冷, 热模拟, 组织演变