Abstract: Martensite  stainless  steel  2Cr13(0. 19C,12.88Cr)was  melted  by  a  vacuum  non-consumable  arc  fumace and 0~0. 18%  Ce was  added  in  casting  ingot.The morphology  and  ingredient  of inclusion  in  steel was  observed  and  analyzed by using optical and scanning electron microscope and X-ray energy dispersive spectrometer.Results showed that with  no-adding rare-earth element Ce the inclusion in steel was irregular MnS,Cr₂S₃ and FeS compound inclusion with dimension  19.33  μm,with  added  0. 14%  Ce  the  inclusion  in  steel  was  compound  rare-earth(RE)inclusion(inner  RE  sulphide  and  outside  RE  silicate)approximated  ellipsoid  with  dimension  18.64   μm  and  with  added  0. 16%～0. 18%  Ce  the  inclu sion  in  steel  was  ellipsoid  or  spheroid  RE  silicate  with  dimension7.69~8.15  μm.

Key words: Rare Earth Element, Stainless Steel 2Cr13, Modification of Inclusion

摘要： 2Cr13(0.19％C、12.88％Cr)马氏体不锈钢由非自耗真空电弧炉冶炼,在铸模加入0～0.18％的Ce。用光学和扫描电镜(SEM)、X-射线能谱仪观察和分析钢中夹杂物形貌和成分。结果表明,未加稀土元素Ce时,钢中夹杂物尺寸为19.33μm的不规则MnS、Cr₂S₃和FeS复合夹杂物;加入0.14％Ce,钢中夹杂物为近似椭球状稀土夹杂物,尺寸18.64μm;复合夹杂物内部为稀土硫化物,外部为稀土硅酸盐;加入0.16％～0.18％Ce时,钢中夹杂物为椭球或球形稀土硅酸盐,尺寸为7.69～8.15μm。

关键词: 稀土, 2Cr13不锈钢, 夹杂物变性