Effect of Nb Content on Structure and Mechanical Properties of High Speed Steel W3Mo2Cr4V(Nb)

Zhang   Yong1,2,Ma   Dangshen2,Liu   Jianhua2,Chen   Zaizhi2，Yong   Qilong1,2   

  1. 1 Kunming University of Science and Technology,Kunming 650093;
    2 Central Iron and Steel Research Institute,Beijing 100081
  • Received:2006-12-27 Online:2007-05-01 Published:2023-02-03

Nb含量对W3Mo2Cr4V(Nb)高速钢组织和力学性能的影响

张永1,2, 马党参2，刘建华2，陈再枝2，雍岐龙1,2   

  1. 1. 昆明理工大学材料与冶金工程学院 
    2. 钢铁研究总院结构材料研究所 
  • 作者简介:张 永(1981-),男，硕士研究生，2007年昆明理工大学毕业，从事高速钢和模具钢的研究。

PDF

Abstract: The  effect  of0～1.5%  Nb  on  structure  and  mechanical  properties  of  steel  W3Mo2Cr4V(0.8~1. 1C,3.8 ~4. 1Cr,2.9~3.2W,1.8~2. 1Mo,1.0~1.3V)melted   by  25 kg vacuum induction funace   has   been studied.   Test   results showed that with increasing Nb content the amount of niobium carbide in cast structure increased; quenching austenite grain  was  refined;  as  quenched  at  1180  ℃,compared  with  HRC  value  of≤0. 1%  Nb  steel  the  HRC  value  of  1.2%~ 1.5%Nb  steel  increased by  6.0; the  secondary hardening  ability  and red hardness  of Nb  steel were  obviously  increased.

Key words: Nb Bearing High Speed Steel W3Mo2Cr4V, Secondary Hardening, Mechanical Property

摘要： 研究了0～1.5％Nb对25 kg真空感应炉冶炼的W3M02Cr4V钢(％:0.8～1.1C、3.8～4.1Cr、2.9～3.2W、1.8～2.1Mo、1.0～1.3V)组织和力学性能的影响。试验结果表明:随着Nb含量提高,铸态组织中铌碳化物增多;淬火奥氏体晶粒变细;1180℃淬火时,1.2％～1.5％Nb钢比≤0.1％Nb钢HRC值提高了6.0;二次硬化能力和红硬性也得到了提高;使钢在较高淬火温度下的机械性能得到改善。

关键词: 含Nb高速钢W3Mo2Cr4V,  ,  二次硬化, 力学性能