Special Steel ›› 2007, Vol. 28 ›› Issue (5): 40-41.

Previous Articles     Next Articles

V-N Microalloyed Modified Containing Tungsten Cr5W Steel for Cold Rolling Working Roll

Wu Jianping1,2 , Jia Jianping1 , Wang Zidong2   

  1. 1. Xingtai Machinery & Mill Roll Co.,Ltd., Sinosteel,Xingtai 054025;
    2. School of Materials Science and Engineering , University of Science and Technology,Beijing 100083;
  • Received:2007-03-28 Online:2007-10-01 Published:2023-02-14

V-N微合金化含钨改型Cr5W冷轧工作辊用钢

武建平1,2， 贾建平1，王自东2   

  1. 1. 中钢集团邢台机械轧辊有限公司，邢台 054025;
    2. 北京科技大学材料科学与工程学院，北京 100083;
  • 作者简介:武建平(1966-)，男，高级工程师，1988年毕业于北京科技大学，从事电渣冶金和材料研究。

PDF

98

Abstract: The modified containing tungsten added V-N microalloying Cr5W tool steel-0.70～0.90C，≤1.00Si，0.20~0.60Mn，4.50~5.50Cr，1.00~1.50W，≤0.15Mo，≤0.3V，300×10-6～350×10-6N has been developed. Test results indicated that the structure of modified Cr5W steel quenched at 960 ℃ was martensite + carbide,of which the average HRC hardness was 63.5,and the average HRC hardness of modified Cr5W steel after temper at 180 ℃ was 63.2 higher than hardness(average HRC 62.3)of 180 ℃ tempered Cr5 steel(0.70~0.90C，≤1.00Si，0.20～0.60Mn，4.50~5.50Cr，0.15~0.70Mo，with 80×10-6～120×10-6N);and with same hardness value the relative wearing resistance of modified Cr5W steel increased by 50% as compared with that of Cr5 steel.

Key words: Modified Cr5W Steel, Tungsten, Cold Rolling Working Roll, V-N Microalloying

摘要： 开发了加V-N合金的含钨改型Cr5W工具钢(%:0.70～0.90C、≤1.00Si、0.20～0.60Mn、4.50～5.50Cr、1.00～1.50W、≤0.15Mo、≤0.3V;300×10-6～350×10-6N)。Cr5W钢960℃淬火后组织为马氏体+碳化物,平均HRC硬度值为63.5,180℃回火后的平均HRC值为63.2,高于Cr5钢(%:0.70～0.90C、≤1.00Si、0.20～0.60Mn、4.50～5.50Cr、0.15～0.70Mo；80×10-6～120×10-6N)180℃的回火硬度(HRC值62.3),在相同硬度下,Cr5W钢的相对耐磨性较Cr5钢提高50%。

关键词: 改型Cr5W钢, 钨, 冷轧工作辊, V-N微合金化