Abstract: Elevated temperature ductility and deformed fracture mechanism of 370 mm×490 mm cast bloom of non-  quenched   and   tempered   free   cutting   steel   38MnVS(%:0.42C,1.29Mn,0.09V,0.067S)have   been   studied   by   Gleeble 1500D   thermal   simulator. Results   showed   that   the   Zero   Strength   Temperature(ZST)and   Zero   Ductility   Temperature (ZDT)of steel  38MnVS were respectively1370 ℃ and1335  ℃;there were  two brittle  zones  for  steel  38MnVS  in  temperature range  from  melting  point  Ts  to  600  ℃  i.e.  brittle zone I-Ts～1250 ℃ and brittle zone Ⅲ 875～600 ℃, therefore the straightening temperature of cast bloom of the steel should be more than 875 ℃.