Abstract: The    effect    of    quenching    temperature1025~1125℃+570℃4    h    air    cooling    +    720    ℃    2    h    air    cooling  and    secondary    tempering    temperature    680~780    ℃    after1050~1075    ℃    quenching    on    mechanical    properties    of    martensite  heat                     resistant                     steel                     X12CrMoWVNbN10- 1- 1(%:0. 11C,10.28Cr,0.77Ni,1.0Mo,0.96W,0. 18V,0.04Nb,0.053N)  has    been    studied.    Results    show    that    with    increasing    quenching    temperature,the    strength    of   steel    increases,of   which    the  plasticity    has    no    appreciable    change,but    the    impact    toughness    obviously    decreases;    with    increasing    tempering    temperature,  the   strength   of   steel   decreases,while   the   plasticity   and   impact   toughness   of   steel   increase.   The   optimizing   heat   treatment   of the     steel     is1050~1075℃1~2h     oil     cooling     +570℃4h     air     cooling     +715~725     ℃     2     h     air     cooling.

摘要： 研究了淬火温度1025～1125℃+570℃4 h空冷+720℃2 h空冷和1050～1075℃淬火后二次回火温度680～780℃对马氏体耐热钢X12CrMoWVNbN10-1-1(%:0.11C、10.28Cr、0.77Ni、1.0Mo、0.96W、0.18V、0.04Nb、0.053N)力学性能的影响。结果表明,随淬火温度的提高,钢的强度增加,塑性变化不大,但冲击韧性显著下降。随回火温度的提高,强度下降、塑性、韧性增加。该钢优化的热处理工艺为:1 050～1 075℃1～2 h油冷+570℃4 h空冷+715～725℃2 h空冷。