Abstract: Hot plasticity of U71Mn steel(%:0.75C,1.20Mn) and U75V steel (%:0.75C,0.94Mn,0.05V,  0.005Al) at   700~1300℃   has   been   studied   by   using   Gleeble- 1500D   thermo-simulation   machine. Results   show   that   as   vanadium   carbo-nitride precipitates   at grain boundary   and inside, the hot plasticity, especially the plasticity   at Ⅲ brittle zone (850℃), of microalloying   heavy   rail   steel   decreases   by   adding   vanadium.   The   strengthening   temperature   of   cast   bloom should be ≥900 ℃ to prevent bloom crack forming.

摘要： 用Gleeble-1500D热模拟试验机研究了U71Mn钢(%:0.75C、1.20Mn)和U75V钢(%:0.75C、0.94Mn、0.05V、0.005Al)700～1300℃的高温塑性。结果表明,由于碳氮化钒在晶界和晶粒内部析出,加钒降低微合金化重轨钢的高温塑性,特别是第Ⅲ脆性区(850℃)的塑性。为防止铸坯裂纹出现,铸坯矫直温度应≥900℃。

关键词: 微合金化重轨钢, 钒, 高温塑性