Abstract: High   temperature   mechanical   properties   of grain-oriented   silicon   steel(0.027%C,3.06%Si) melting   by a  30 kg vacuum induction furnace  in lab and simulating 50mm thin slab casting and rolling process have been tested by Gleeble- 1500D   stress/strain   thermal   simulation   machine.Results   show   that   with   strain   rate   1×10^-3s^-1,there   are   two  brittle  temperature zones for  the  test  steel,i.e.  I  brittle  zone-  melting  point  to  1300  ℃  and  Ⅲ  brittle  zone-  800～600 ℃. 1390~1410  ℃ is  crack  sensitive  range  of the  test  steel.  In  I brittle  zone  the  dentritic  crystal boundary  surrounded by liquid  film  of  rich  solute  is  main  reason  to  produce  brittlement.And  in  Ⅲ  brittle  zone,γ→α  transformation,y,α  and  Fe₃C triple phase coexistence at about 760 ℃ and precipitates at grain boundary are main cause of deterioration in ductility.

摘要： 采用Gleeble-1500D应力/应变热模拟试验机,对实验室30 kg真空感应炉冶炼的模拟50 mm薄板坯连铸连轧流程生产的取向硅钢(0.027%C,3.06%Si)进行了高温力学性能测试。结果表明,在1×10^-3s^-1应变速率下,所测试的试验钢存在两个脆性温度区,即熔点至1 300℃的第Ⅰ脆性区和800～600℃的第Ⅲ脆性区。1390～1410℃是试验钢的裂纹敏感区间。在第Ⅰ脆性区,高温下树枝晶界面被富集溶质的液相膜包围是产生脆性的主要原因。在第Ⅲ脆性区,γ→α转变和760℃左右γ、α和Fe₃C三相共存以及晶界析出物,是造成塑性恶化的主要原因。