Abstract: Effect    of   0.09%~0. 14%    C    content    on    structure    and    mechanical    properties    of   2Mn-0.003B-0.05Ti    micro- alloying   steel   cold   drawn   with   5%~50%   reduction   and   aged   at   100~500   ℃   for   2   h   has   been   studied.   Results   show   that with    lower    carbon    content (0.09%~0. 12%C), the    finer    and    uniform    distributed    granular    bainite    structure    in    steel    is    obtained, while    with    0. 14%    C, the    lumpy    ferrite    shall    occur    in    structure; at    same    cold-drawing    reduction, with    increasing carbon   content   the   strength   of   steel   increases   and   plasticity   decreases, and   the   larger   the   reduction, the   more   significant   the tendency; and   with   increasing   carbon   content   the   increment   of   strength   of   steel   aged   obviously   decreases.

Key words:  , Mn-B-Ti Cold-Hardening Microalloying Steel, Carbon Content, Granular Bainite, Mechanical Properties

摘要： 研究了0.09%～0.14%C含量对5%～50%冷拔减面率和100～500℃2 h时效处理的2Mn-0.003B-0.05Ti非调质钢组织和力学性能的影响。结果表明,当碳含量较低(0.09%～0.12%C)时,可获得比较细小均匀的粒状贝氏体组织,但当碳含量为0.14%时,则组织中出现块状铁素体;在相同的拉拔减面率下,随着碳含量的增加,该钢的强度提高,塑性降低,当减面率较大时,这种差别比较明显;随着碳含量的升高,时效处理后的该钢强度增量明显降低。

关键词:  Mn-B-Ti冷作强化非调质钢, 碳含量, , 粒状贝氏体, 力学性能