Abstract: Test  steels were melted  by a 25 kg  vacuum   induction   furnace   in   argon  protective  atmosphere  with  charging  of      austenite heat  resistant  steel  TP347H (0.07C,17.98Cr,10.78Ni,0.70Nb,0.0267N) for super critical pressure  boil- er  and  adding 0~0. 16%B. Results  showed  that  as  added  ≥0.02%B  the  austenite  grain of  test  steel  obviously  coarsened and   forging   billet  of  steel  cracked  as  forging   at   1200～950   ℃;as  added   about  0.01%B the austenite  heat  resistance   steel  has   optimum  comprehensive  properties   i.e. tensile   strength  of  steel   at   ambient   was  615  MPa,the   stress-rupture  life  and   e- longation  of  steel  with  120 MPa  at  750   ℃  were  respectively  230  h  and  42%.

摘要： 试验钢以超临界锅炉用奥氏体耐热钢TP347H(%:0.07C、17.98Cr、10.78Ni、0.70Nb、0.0267N)为炉 料，用25 kg真空感应炉在氩气保护下熔炼，并加入0～0.16%B。结果表明，当加B量≥0.02%时，试验钢奥氏体 晶粒明显粗化，1200～950℃锻造时锻坯开裂。当加B量约0.01%时，奥氏体耐热钢TP347H具有最佳的综合性 能：钢的室温抗拉强度为615 MPa;750 ℃,120 MPa钢的持久寿命为230 h,伸长率为42%。

关键词: 奥氏体耐热钢 , TP347H , 加硼 , 组织 , 性能