Abstract: The  process  of thin  slab  produced  by  FTSR(Flexible  Thin  Slab  Rolling)process  has  been  simulated  by Gleeble-3500  thermal  simulation  machine,and  the  high  temperature  plasticities  of  slab  of  steel  SS330(0.06%C)and  steel SS400(0.20%C)600～1350  ℃  were  tested,Results  showed  that  the  high  temperature  plasticity  of  steel  SS400  at  700~ 900 ℃ was high than that of steel  SS330;the high temperature plasticity decreasing of steel  SS400 due to segregation and accumulation of sulphide and oxide at boundary of columnar crystal caused inner cross crack formation in slab. With con trolling   sulphur  content  in   steel  decreasing  to  0.010%  from  0.015%,total  oxygen  content  to  30×10^-6 from  45×10^-6,  superheating  degree  of  molten  steel  to 20~35℃  from 30~50℃,Mn/S  in  steel  ≥60  and  modifying  slab  casting  speed  to 3.0~4.5  m/min  from  original 2.5~6.0  m/min  with  reasonably  controlling  secondary  cooling  water  amount, the  thin  slab inner cross crack was avoided effectively.

Key words: FTSR Process,Steel SS400,Thin Slab,Inner Cross Crack,Forming Mechanism

摘要： 采用Gleeble-3500热模拟机模拟FTSR薄板坯生产工艺,试验了SS330钢板坯(0.06％C)和SS400钢板坯(0.20％C)在600～1 350℃的高温塑性。结果表明,SS400钢在700～900℃的高温塑性高于SS330钢,SS400钢板坯内部产生的横向裂纹是由于柱状晶晶界处硫、氧化物的偏聚,使钢晶界的高温塑性下降所致。通过钢中硫含量由0.015％降低至0.010％,全氧含量由45×10^-6降至30×10^-6,钢中Nn／S≥60,钢水过热度由30～50℃降至20～35℃,铸坯拉速由2.5～6.0 m／min改为3.0～4.5 m／min,控制二冷水量,有效地避免了薄板坯内部横裂纹的产生。

关键词: FTSR工艺, SS400钢, 薄板坯, 内部横裂纹 , 形成机理