Special Steel ›› 2007, Vol. 28 ›› Issue (3): 25-27.

Previous Articles     Next Articles

Effect of Holding Technology at Intermediate Roll Table in Hot Continuous Rolling on Phase Transformation and Structure of Low Carbon Steel

Xu  Yuanjun1,Zhao   Gang1,Wen   DunWei2，Gangcheng2   

  1. 1 Materials and Metallurgy College,Wuhan University of Science and Technology,Wuhan 430081;
    2 Wuhan Iron and Steel Corp,Wuhan 430083
  • Received:2006-11-15 Online:2007-05-01 Published:2023-01-31

热连轧中间辊道保温工艺对低碳钢相变和组织的影响

徐远军1，赵刚1，温盾2，魏钢城2   

  1. 1武汉科技大学材料与冶金学院，武汉430081;
    2武汉钢铁公司，武汉430083
  • 作者简介:徐远军(1981-),男，硕士研究生，2004年武汉科技大学材 料成型与控制专业毕业，从事轧制过程组织演变和计算机模 拟控制研究。

PDF

Abstract: The continuous  cooling  transformation(CCT)curves  of  low  carbon  steel Q235(0. 15C,0.005B)with  1050℃30%   deformation, holding   10,40,90s and  cooling  to 1000℃30%   deformation   then   cooling   with 5℃/s   to 880℃  and  cooling  with1,5,15  and  25℃/s  have  been  measured  using  dilatometry  by  Thermecmastor-Z  thermal  simulation machine.  With  prolonging  holding  time  at  intermediate  roll  table, the  CCT  phase  transformation  beginning  and  finishing  curves moved down to right and grain size of steel at ambient gradually enlarged.

Key words: Steel Q235,Hot Continuous Rolling,Intermediate Roll Table,Holding,CCT Curves,Structure

摘要： 利用膨胀法在Thermecmastor-Z热模拟实验机上测定了低碳钢Q235(％:0.15C、0.005B)1 050℃30％变形后经10,40,90 s保温冷却至1 000℃30％变形,5℃/s冷却至880℃,然后以1,5,15,25℃/s速度冷却的连续冷却转变(CCT)曲线。随中间辊道保温时间的延长,连续冷却相变开始和结束曲线均向右下方移动,并且钢的室温晶粒逐渐变大。

关键词: Q235钢, 热连轧, 中间辊道, 保温, CCT曲线, 组织