Effect of Inclusion and Structure on Low Temperature Impact Toughness of 20R Steel

王勇; 苏春霞; 张起生

您当前的位置：

首页 >

文章列表页 >

Effect of Inclusion and Structure on Low Temperature Impact Toughness of 20R Steel

更新时间：2026-01-21

- Effect of Inclusion and Structure on Low Temperature Impact Toughness of 20R Steel
- Special Steel Vol. 28, Issue 6, Pages: 30-31(2007)
- 作者机构：
  
  鞍钢股份有限公司技术中心,鞍山,114001
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：18 June 2007，
  
  Online First：27 December 2022，
  
  Published：27 December 2007
- 稿件说明：
移动端阅览
王勇, 苏春霞, 张起生. Effect of Inclusion and Structure on Low Temperature Impact Toughness of 20R Steel[J]. Special Steel, 2007, 28(6): 30-31.
DOI：

王勇, 苏春霞, 张起生. Effect of Inclusion and Structure on Low Temperature Impact Toughness of 20R Steel[J]. Special Steel, 2007, 28(6): 30-31. DOI：

摘要

在实验室用200kg真空感应炉和500mm轧机研究了成分(%)为0.15C、0.008P、0.008S、0.06Mo和0.18C、0.009P、0.004S、0.01Mo两种20R钢纯净度和轧制工艺对低温冲击性能的影响。结果表明

降低钢中S含量和夹杂物可明显改善钢的低温冲击韧性:钢在1180℃加热、1020℃开轧和800℃终轧的情况下

0.008%S钢热轧空冷态和热轧+880℃正火态的-40℃纵、横向冲击功分别为14.7 J、10 J和13 J、9 J

钢中夹杂物为A类1.5级

B类1.5级;0.004%S钢热轧空冷后-40℃纵、横向冲击功分别为180 J、98 J

钢中夹杂物为D类0.5级;0.004%S钢经热轧后控冷(水冷)

带状组织改善

-40℃纵向和横向冲击功分别增至210 J和146 J。

Abstract

The effect of cleanliness and rolling process of two heats of 20R steel-0. 15C

0.008P

0.008S

0.06Mo and 0. 18C

0.009P

0.004S

0.01Mo on low temperature impact energy of steel has been rescarched by 200 kg vacuum induction furnace and 500 mm mill in laboratory.Results showed that the low temperature impact toughness of steel was obviously improved by decreasing S content and inclusion; with steel1180 ℃ heating

1020 ℃ beginning rolling and 800 ℃ finishing rolling

the longitudinal

cross impact energy at -40℃ of0.008% S steel by hot rolled air cooling and hot rolled + 880 ℃ normalizing were respectively 14.7J

10J and 13J

and inclusion rating in steel was A- 1.5 and B- 1.5; the longitudinal

cross impact energy at -40℃ of 0.004% S steel by hot rolled air cooling were 180J

98 J

and inclusion rating in steel was D-0.5;The longitudinal and cross impact energy at -40℃ of0.004% S steel by hot rolled and control cooling(water cooling)increased respectively to 210 J and 146 J with improved bending structure.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect on Fatigue Failure Behavior Induced by Inclusions in GCr15 Bearing Steel Under Different Metallurgical Processes

High Temperature Mechanical Properties and Fracture Mechanism of 9Cr-2W-3Co Martensitic Heat-resistant Steel

Effect of LF Soft Bubbling Time on Inclusions in Tire Cord Steel LX82 A

The Metallurgical Mechanisms of Inclusions in the FGH4096 Alloy during Electron Beam Refining

Numerical Simulation and Industrial Experiment of Vacuum Arc Remelting

ϕ

690 mm Large-sized GH4738 Superalloy Ingot

Related Author

Wang Zheng

Chen feng

Shi Tao

Yin Qing

Hu Bin

Luo Haiwen

Geng Wei

Zhu Zhibao

Related Institution

School of Metallurgy and Ecological Engineering， University of Science and Technology Beijing

Changzhou Baoling Heavy & Industrial Machinery Co.， Ltd.

Daye Special Steel Co.， Ltd.

Jiangying Xingcheng Special Steel Works Co.， Ltd.， Jiangying

State Key Laboratory of Advanced Refractories， Wuhan University of Science andTechnology

⁰