An Analysis on Mechanism of Insulating Coating's Stripping of Non-oriented Silicon Steel

更新时间：2026-01-21

- An Analysis on Mechanism of Insulating Coating's Stripping of Non-oriented Silicon Steel
- Special Steel Vol. 28, Issue 6, Pages: 32-34(2007)
- 作者机构：
  
  1. 上海交通大学金属基复合材料国家重点实验室,上海,200030
  2. 宝山钢铁股份有限公司,上海,201900
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：26 June 2007，
  
  Online First：27 December 2022，
  
  Published：27 December 2007
- 稿件说明：
移动端阅览
吴树建, 储双杰, 孙宝德, et al. An Analysis on Mechanism of Insulating Coating's Stripping of Non-oriented Silicon Steel[J]. Special Steel, 2007, 28(6): 32-34.
DOI：

吴树建, 储双杰, 孙宝德, et al. An Analysis on Mechanism of Insulating Coating's Stripping of Non-oriented Silicon Steel[J]. Special Steel, 2007, 28(6): 32-34. DOI：

摘要

通过所建立的厚涂层附着模型和电子探针微区分析仪(EPMA)、辉光放电光谱仪(GDS)

分析和研究了无取向硅钢绝缘涂层剥离前后的形貌和成分。结果表明

涂层和基板为物理附着

产生剥离的主要形式为涂层与基板的界面剥离

同时伴有涂层自身的层间剥离;弯曲产生的涂层龟裂可能是导致剥离的一个重要原因。

Abstract

The morphology and component of insulating coating of non-oriented silicon steel before and after stripping have been analyzed and studied by established adhesive model of thick coating

electron probe micro analyzer(EPMA)and glow discharge spectroscopy(CDS).Results showed that the adhesion mechanism of insulating coating with non-oriented silicon steel was physical

the main stripping form was interface stripping between substrate and coating which was accompanied coating's interlaminar stripping.Rimous crack caused by bending may be an important cause for stripping.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Evolution of Asynchronous Cold Rolling Texture in Thickness Direction of Non-Oriented Silicon Electric Steel

Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel

Effect of Cr on Magnetic Properties of Non-Oriented Silicon Steel

Effect of Original Structure of Hot Rolled Plate on Texture Evolution of Cold Rolled Non-Oriented Silicon Steel

Related Author

张正贵

刘沿东

左良

王福

董爱锋

苗晓

申毅

张文康

Related Institution

东北大学材料与冶金学院

沈阳大学机械工程学院材料系

太原钢铁(集团)冇限公司技术中心

武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室

宝山钢铁股份有限公司硅钢部

⁰