Analysis on Corner Cracks of Angle Steel Q420C Rolled from 180 mm x 180 mm Cast Billet and Process Improvement

更新时间：2026-01-21

- Analysis on Corner Cracks of Angle Steel Q420C Rolled from 180 mm x 180 mm Cast Billet and Process Improvement
- Special Steel Vol. 38, Issue 2, Pages: 48-52(2017)
- 作者机构：
  
  1. 钢铁研究总院冶金工艺研究所,北京,100081
  2. 河北钢铁集团唐山钢铁有限责任公司,唐山,063000
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：17 October 2016，
  
  Online First：23 July 2022，
  
  Published：23 July 2017
- 稿件说明：
移动端阅览
赵斌, 崔怀周, 汪成义, et al. Analysis on Corner Cracks of Angle Steel Q420C Rolled from 180 mm x 180 mm Cast Billet and Process Improvement[J]. Special Steel, 2017, 38(2): 48-52.
DOI：

赵斌, 崔怀周, 汪成义, et al. Analysis on Corner Cracks of Angle Steel Q420C Rolled from 180 mm x 180 mm Cast Billet and Process Improvement[J]. Special Steel, 2017, 38(2): 48-52. DOI：

摘要

电力铁塔用18 mm厚160角钢Q420C（/%:≤0.20C

1.00~1.70Mn

≤0.55Si

≤0.035S

≤0.035P

0.020.20V

≥0.015Als）的冶金流程为80 t BOF-LF-CC-车制工艺。利用光学显微镜、SEM以及能谱分析仪对热轧角钢角部裂纹进行了分析

结果表明

裂纹周围存在脱碳层及铁素体膜

裂纹处发现S富集及在晶界析出的AlN破坏了钢基体的连续性;得出连铸振痕谷底的夹渣、成分偏析

热应力和弯曲矫直应力导致了角钢沿晶界开裂。通过降低[N]至0.0080%

控制Als 0.017%~0.022%

Mn/S≥80

钢水过热度≤25℃

保护渣牯度0.73 Pa·s

矫直温度≥950℃等工艺措施

使连铸坯的优质品率由原25.78%提高至85%

有效地降低了角钢角部裂纹的发生。

Abstract

The metallurgical flowsheet of 160 angle steel Q420C with 18 mm thickness for power tower (/% : ≤0.20C

1.00〜1.70Mn

≤0.55Si

≤0.035S

≤0.035P

0.02~0.20V

≥0.015Als) is 80 t BOF-LF-CC-rolling process. The analysis on comer cracks of hot-rolled angle steel is carried out by optical microscope

scanning electron microscope and energy dispersive spectroscopy. The results show that there are decarburized layer and ferrite film around cracks

the S enrichment near cracks and the AIN precipitates at grain boundary are found that break the continuity of steel matrix. It is obtained that the slag inclusions at oscillation mark bottom

segregation

thermal stress and bending straightening stress lead to angle steel crack along grain boundary. With process measures including decreasing [N] to 0.0080%

controlling Als 0.017%~0.022%

[Mn]/[S] ≥80

liquid over heating extent ≤25°C

viscosity of mold powder 0.73 Pa·s

and straightening temperature ≥950°C

the quality cast billet increases to 85% from original 25.78%

it is available to decrease the occurrence of comer cracks of angle steel.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Microstructure and Homogenization Process of Large Ingot of As-cast Condition C650R Nickel-based Alloy

Influence Factors on σ-Phase Precipitation of FeCr16 Corrosion-resistant Soft Magnetic Alloy

Analysis of Surface Defects of High Strength Welding Wire Steel N2M2T Continuous Casting Billet and Process Improvement

Key Technology and Application of Wire Rod Uniformity for MT Grade Steel Cord

Thermodynamic Simulation of Solidification and Precipitation of Cast Duplex Stainless Steel CD3MWCuN

Related Author

Kou Jinfeng

He Yixuan

Li Jinshan

Zhang Bingbing

Zhang Xin

Nie Yihong

Bai Yaguan

Zhu Yincun

Related Institution

Tianjin Heavy Industries Research & Development Co.， Ltd.

Northwestern Polytechnical University， Xi´an

Technical Center ， Baowu Special Metallury Co.， Ltd.

School of Materials Science and Engineering，Shanghai University

Technical Center，Qingdao Branch of CITIC Pacific Steel Research Institute

⁰