Φ16 mm GCr15轴承钢棒材KOCKS轧机热连轧工艺数值模拟和分析

李小龙; 程卫国; 周立新; 周敦世; 邹晖

您当前的位置：

首页 >

文章列表页 >

Φ16 mm GCr15轴承钢棒材KOCKS轧机热连轧工艺数值模拟和分析

试验研究 | 更新时间：2026-01-21

- Φ16 mm GCr15轴承钢棒材KOCKS轧机热连轧工艺数值模拟和分析
- Numerical Simulation and Analysis on Hot Continuous Rolling Process of KOCKS Mill for Φ16 mm GCr15 Bearing Steel Bar
- 特殊钢 2016年37卷第5期页码：5-9
- 作者机构：
  
  1. 大冶特殊钢股份有限公司中棒厂,黄石,435001
  2. 高品质特殊钢湖北省重点实验室,黄石,435001
- 作者简介：
  
  [ "李小龙(1983-)，男，硕士(2012年南昌大学)，工程师，轧钢工艺技术和材料加工计算机数值模拟。" ]
- 基金信息：
- DOI：
  中图分类号：
- 收稿：2016-04-07，
  
  网络首发：2022-07-27，
  
  纸质出版：2016-07-27
- 稿件说明：
移动端阅览
李小龙, 程卫国, 周立新, 等. Φ16 mm GCr15轴承钢棒材KOCKS轧机热连轧工艺数值模拟和分析[J]. 特殊钢, 2016,37(5):5-9.

李小龙, 程卫国, 周立新, et al. Numerical Simulation and Analysis on Hot Continuous Rolling Process of KOCKS Mill for Φ16 mm GCr15 Bearing Steel Bar[J]. Special Steel, 2016, 37(5): 5-9.
李小龙, 程卫国, 周立新, 等. Φ16 mm GCr15轴承钢棒材KOCKS轧机热连轧工艺数值模拟和分析[J]. 特殊钢, 2016,37(5):5-9. DOI：

李小龙, 程卫国, 周立新, et al. Numerical Simulation and Analysis on Hot Continuous Rolling Process of KOCKS Mill for Φ16 mm GCr15 Bearing Steel Bar[J]. Special Steel, 2016, 37(5): 5-9. DOI：

摘要

采用DEFORM-3D三维大变形热力耦合弹塑性有限元软件对Ф21.5 mm GCr15轴承钢坯料在四架KOCKS轧机连轧成Φ16 mm棒材工艺过程进行了数值模拟。分析了棒材在KOCKS轧机孔型中轧制时的等效应力、等效应变、温度场以及轧制力等轧制工艺参数。结果表明，棒材在KOCKS机组中的变形主要发生在延伸孔型，精轧孔型的变形量较小，尤其在最后一道次；棒材在KOCKS机组中的宽展是不均匀，在靠近轧辊的区域宽展较小，在辊缝处宽展较大并产生鼓形;棒材在KOCKS机组中等效应变已达到芯部渗透，这对保证组织致密度和成品内部质量是非常有利的，现场各道次轧制力的实测值与模拟值的相对误差＜2%。

Abstract

The numerical simulation of process of four stand tandem KOCKS mill continuous rolling Ф16 mm GCr15 bearing steel bar from Ф21.5 mm stock has been carried out by using DEFORM-3D three-dimensional heavy deformation thermal-mechanical coupled with elastic-plastic finite element software. And the rolling process parameters for stock rolling in KOCKS mill roll pass including equivalent stress

equivalent strain

temperature field and rolling force of steel are analyzed. Results show that the deformation of steel bar in KOCKS mill occurs mainly at rough rolling passes

and that at finish passes is small

especially at last pass ； the spread of steel bar in KOCKS mill stands is uneven

that near the roller area is smaller and that near the roll gap is larger to form bulge ； and in KOCKS mill stands the equivalent strain reaches the center of steel bar

it is available to ensure the compact density of structure and internal quality of finishing products. The relative error between simulated value and measured value of rolling force at each pass in situ is less than 2%.

关键词

Keywords

references

浏览量

下载量

CSCD

CNKI被引量

文章被引用时，请邮件提醒。

提交

工具集

关联资源

EH420海工钢80 mm特厚板堆垛缓冷数值模拟

4J36因瓦合金钢锭凝固组织的数值模拟研究

基于ABAQUS的X70管线钢连铸板坯空冷的热力耦合分析

ϕ

690 mm大尺寸GH4738合金真空自耗重熔数值模拟与工业试验

1Cr16Co5Ni2MoWVNbN耐热钢球座模锻成型工艺模拟与试验验证