Abstract: The quenched and tempered structure, mechanical properties and corrosion resistance of two Cr17Mo type corrosion resistant stainless steels for plastic mould-0.39C,0.70Ni,16.73Cr,1.07Mo and 0.53C,1.05Ni,16.87Cr,0.96Mo have been tested and researched. As the carbon content in Cr17Mo type steel increased from 0.39% to 0.53%,the peak HRC hardness value of steel quenched at 1060 ℃ and tempered at 475 ℃ increased from 46.5 to 53.4;and the two test steels had better corrosion resistance in weak acid, oxidizing acid and 1% HCl.

摘要： 试验研究了成分(％)为:0．39C,0．70Ni,16．73Cr,1．07Mo和0．53C,1．05Ni,16．87Cr,0．96Mo两种Cr17Mo型耐蚀塑料模具钢的淬回火组织、力学性能和耐蚀性能。试验结果表明,当Cr17Mo型钢中碳含量由0．39％提高至0．53％时,经1 060℃淬火,475℃回火后该钢的峰值硬度HRC值由46．5提高到53．4;两种试验钢在弱酸、氧化性酸和1％盐酸中均有较高的耐腐蚀性能。