Abstract: The φ140～170  mm  bars  of steel  37CrMnMo(0.35～0.38C,0.85～1.00Mn,0.90～1.20Cr,0.28~ 0.33Mo,≤0.015P,≤0.008S)for   coupling   sleeve   of  petroleum   drill   stem   are   produced   by   50t   EBT   arc   furnace-LF (VD)-Al  and  Ca-Si  wire  feeding-3.16  t  ingot  casting-800/650×4  mills  rolling  flow  sheet  at  Benxi  steel. Analyais  and  examination   results   showed   that   hydrogen   content   in   steel   products   was (0.5～1)×10^-6,oxygen   content(8～20)×10^-6,nitrogen    content(55～90)×10^-6,inclusion rating 0~2, J₂₅  hardenability HRC value 42~51, transversal  impact  energy   at  - 10℃ 56~218J, longitudinal   impact   energy   at   - 10℃ 76~233  J and   the   strength   and   plasticity   of  products all met the requirement of standard.

Key words: Steel 37CrMnMo,LF(VD),Wire Feeding,Mechanical Properties

摘要： 本钢采用50 t偏心底电弧炉熔炼-LF(VD)-喂Al和Ca-Si线-3.16 t铸锭-800/650×4轧机流程生产Φ140～170 mm石油钻杆连接套用37CrMnMo钢(％:0.35～0.38C、0.85～1.00Mn、0.90～1.20Cr、0.28～0.33Mo、≤0.015P、≤0.008S)。检验结果表明,钢材中H含量(0.5～1)×10^-6,O含量(8～20)×10^-6,N含量(55～90)×10^-6,夹杂物0～2级,J₂₅淬透性HRC值42～51,-10℃横向冲击功56～218 J,-10℃纵向冲击功76～233 J,强度和塑性均满足标准要求。

关键词: 37CrMnMo钢, LF(VD) ,  , 喂丝 , 力学性能