Abstract: The  effect  of austenitizing  at  880～900  ℃,and  austempering  at 280～340  ℃ in  salt bath  on mechanical properties   and   wear   resistance   of  as-cast   low   alloy   austenite-bainite   steel   38CrMnSi2RE(%:0.35～0.42C,1.5~2.0Si, 1.0~1.5Mn,1.0Cr 、0.2RE)for  carterpillar  band  of tractor  has  been  studied.  Test  results  indicated  that  the  optimum  heat treatment process was austenitizing at 880～900 ℃ and austempering at 310 ℃ for 60 min to get the tensile strength of steel ≥1100MPa,elongation   =7.9%,HRC   hardness   value≥44,impact   value≥88   J/cm² .The   service   life   of   as-cast   steel 38CrMnSi2RE carterpillar band was  1.69 time as long as that of steel ZGMn13.

Key words: Carterpillar , Band,Austenite-bainite , Steel , 38CrMnSi2RE,Austempering,Mechanical , Properties, Wear Resistance

摘要： 研究了880～900 ℃奥氏体化，280～340 ℃盐浴等温淬火对拖拉机履带用铸态低合金奥氏体-贝氏体 钢38CrMnSi2RE(%:0.35~0.42C 、1.5~2.0Si 、1.0~1.5Mn 、1.0Cr,0.2RE)力学性能和耐磨性的影响。试验结果 表明，38CrMnSi2RE钢最佳热处理工艺为880～900 ℃奥氏体化，310℃等温60 min。该钢抗拉强度≥1100 MPa,伸 长率=7.9%,HRC硬度值≥44,冲击值≥88 J/cm²。38CrMnSi2RE钢履带板的使用寿命为ZGMn13钢的1.69倍。

关键词: 履带板 奥氏体-贝氏体钢38CrMnSi2RE等温淬火力学性能 耐磨性