Abstract:  Rolling        test        on        steel        plate(0.09C,0. 12Si,0.98Mn,0.010P,0.005S,0.010Nb,0.04Als)for        wheel spoke  with  finishing  rolling  temperature  830～890  ℃  and  coiling  temperature  620～680  ℃  has  been  carried  out  by 1700mm  hot  rolling  mill  train.  Results  showed  that  with  slab  heating  temperature  1230~1250  ℃,finishing  rolling  tem- perature  870±15℃,coiling  temperature  660±15  ℃,the  structure  of  steel  plate  for  wheel  spoke  was  fine  ferrite  +  minor pearlite,the   yield   strength   of   steel   was   335～380MPa,tensile   strength   430～485MPa,elongation   26%~31%,the   longitudinal  strength  difference  of each  steel  coil  was  13~37MPa,and  the  punching  formability  during  vehicle  wheel  manufacturing  was  excellent  with  punching  rejection  rate  less  than  0.3%.

摘要： 通过1700 mm热连轧机组对轮辐钢(%:0.09C、0.12Si、0.98Mn、0.010P、0.005S、0.010Nb、0.04Als)进行830～890℃终轧温度和620～680℃卷取温度的轧制试验。结果表明,板坯加热温度1230～1250℃、终轧温度(870±15)℃、卷取温度(660±15)℃生产的车轮用轮辐钢板的组织为细铁素体加少量的珠光体,屈服强度335～380 MPa,抗拉强度430～485 MPa,伸长率26%～31%,每卷带钢的纵向强度差为13～37 MPa,在车轮制作过程中冲压成型良好,冲废率小于0.3%。