Abstract: Structure  and  mechanical  properties  of0. 15C- 1.5Mn- 1.5Al-0.3Si  TRIP  steel  heated  at  820  ℃  for  2  min then quenching  in  450  ℃  salt bath  for  5~300  s,air  cooling  have  been  studied.  Results  showed  that  with  increasing  iso- thermal-time  in  Bainite  transformation  field  at  450  ℃,the  yield  strength  and  elongation  of steel  increased  while  tensile strength  decreased, and  the  product  of tensile  strength-elongation  of  steel  was  highest  i.e.23000  MPa%  with  isothermal- treating  for  60  s; as  isothermal-treating  for  less  than  60  s, with  increasing  isothermal-treating  time, the  retained  austenite content  in  steel  increased, as  isothermal-treating  for  more  than  60  s, with  increasing  isothermal-treating  time, the  retained austenite content in  steel decreased, and the retained austenite content in  steel isothermal-treating for 60  s was highest i.e.  14%.

摘要： 研究了0.15C-1.5Mn-1.5Al-0.3Si TRIP钢820℃2 min加热后快冷至450℃盐浴中保温5～300s空冷的组织和力学性能。结果表明,随在贝氏体转变区450℃等温时间的增加,该钢的屈服强度和伸长率增加,抗拉强度降低,等温时间60s时强塑积最佳,为23 000MPa%;等温时间≤60s时随等温时间增加钢中残余奥氏体含量增加,>60s时随等温时间的增加钢中残余奥氏体含量降低,60s时钢中残余奥氏体达到最高值,为14%。