Abstract: With  using  60%  hot  metal  +  quality  scrap  charge,Consteel  EAF  eccentric  bottom  tapping  operation,con- trolling    tapping    end [C]    0.035%～0.050%    and    tapping[P]≤0.012%,LF    refining    by    low    basicity    slag,feeding silicon  wire,  soft  blown  argon  for  15  min  after  LF  refining  and  fully  shielding  auto  control  casting  150  mmx150  mm  bilet  in whole period,  the  average oxygen  content  in steel  H11Mn2SiA(0.06~0.09C,0.82～1.00Si,1.45~1.70Mn)for welding  wire  was  20×10^-6,of which  the  Φ5.5  mm  wire  rods  could  be  direct  drawn  to  φ1.0  mm  wire  without  by  heat  treatment and  no-broken  wire   occurred.

摘要： 采用60％铁水+优质废钢,Comteel电弧炉偏心底炉出钢留渣作业,控制出钢终点[C]0.035％～0.050％、出钢[P]≤0.012％;LF用低碱度渣精炼,喂硅钙线,LF精炼后软吹氩15 min;150 mm×150 mm方坯连铸时,采用全保护自动控制浇铸和结晶器、铸坯凝固末端电磁搅拌,使所生产的H11Mn2SiA焊线钢(％:0.06～6.09C、0.82～1.00Si、1.45～1.70Mn)的平均氧含量为20×10^-6,Φ5.5 mm盘条不经热处理可直接冷拔至Φ1.0 mm不断丝。

关键词: H11Mn2SiA焊线钢, Consteel EAF, LF氧含量