Effect of Carbon and TiO₂ on Fluidity of Mold Flux

Special Steel ›› 2006, Vol. 27 ›› Issue (5): 15-17.

Previous Articles Next Articles

Effect of Carbon and TiO₂ on Fluidity of Mold Flux

Wu Shoufang¹,Li Hong¹,Wang Gongliang², Liang Mei²

1 School of Metallurgical and Ecological Engineering,University of Science and Technology,Beijing 100083;
2 Shijiazhuang Iron and Steel Co, Shijiazhuang 050031

Received:2006-04-07 Online:2006-10-01 Published:2006-10-01

碳和TiO₂对保护渣流动性的影响

武守防¹, 李宏¹, 王恭亮², 梁玫²

1北京科技大学冶金与生态工程学院，北京100083;
2石家庄钢铁公司，石家庄050031

作者简介:武守防(1976-),男，硕士研究生，从事连铸工艺和质量研究

Abstract

Abstract: The effect of C content(8.39%~14.20%)and TiO₂(0.35%) on fluidity of mold flux-21.98~ 27.93 CaO,32.03～43.20 SiO₂,4.58~5.83 Al₂O₃ at 1120～1200℃has been studied.The results showed that residual carbon in flux and TiO₂ in flux which was produced by Ti oxidation in Ti bearing steel led to worse fluidity of mold flux

摘要： 研究了碳含量(8.39%～14.20%)和TiO₂ (0.35%) 对主要成分(%)为21.98～27.93CaO, 32.03～43.20SiO₂,4.58~5.83Al₂O₃ 保护渣在1120~1200℃时流动性的影响。结果表明，液态保护渣有剩余碳以及含钛钢中的Ti氧化生成TiO₂ 进入保护渣后均会恶化保护渣的流动性能

关键词: 结晶器保护渣, 碳, TiO?, , 流动性

Wu Shoufang, Li Hong, Wang Gongliang, Liang Mei. Effect of Carbon and TiO₂ on Fluidity of Mold Flux[J]. Special Steel, 2006, 27(5): 15-17.

武守防, 李宏, 王恭亮, 梁玫. 碳和TiO₂对保护渣流动性的影响[J]. 特殊钢, 2006, 27(5): 15-17.

Effect of Carbon and TiO₂ on Fluidity of Mold Flux

碳和TiO₂对保护渣流动性的影响

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 0

Recommended Articles

Metrics

Comments