Process Practice for Increasing Lining Life of 45 t AOD Units

Special Steel ›› 2006, Vol. 27 ›› Issue (2): 56-57.

Previous Articles Next Articles

Process Practice for Increasing Lining Life of 45 t AOD Units

Wang Guiping , Fan Hongjun

Taiyuan Iron and Steel(Group)Co Ltd,Taiyuan 030003

Received:2005-10-16 Online:2006-04-01 Published:2023-03-02

提高45t AOD炉龄的工艺实践

王贵平，范红军

太原钢铁(集团)有限公司，太原 030003

作者简介:王贵平(1975-),男，硕士，工程师，2003年东北大学毕业，从事不锈钢品种、工艺研究。

Abstract

Abstract: With using magnesitc-calcium brick as lining material of 45 t AOD refining units at Taiyuan Steel to replace magnesite-chrome brick,establishing available AOD line baking procedure,shortening refining time,and controling slag basicity CaO/SiO₂=1.8~2.0,(CaO+MgO)/SiO₂=2.0~2.4,the 45 t AOD lining life has been increased to 189 heats from 50 heats.

Key words: AOD, Refining, Line Life, Process

摘要： 通过采用镁钙砖取代镁铬砖作为太钢45 t AOD精炼炉的炉衬材料,制定合理的AOD炉衬烘烤制度,缩短精炼时间,控制炉渣碱度CaO/SiO₂=1.8~2.0,(CaO+MgO)/SiO₂=2.0~2.4,使45 t AOD炉龄由50炉次提高到189炉次。

关键词: AOD, 精炼, 炉龄, 工艺

Wang Guiping , Fan Hongjun. Process Practice for Increasing Lining Life of 45 t AOD Units[J]. Special Steel, 2006, 27(2): 56-57.

王贵平, 范红军. 提高45t AOD炉龄的工艺实践[J]. 特殊钢, 2006, 27(2): 56-57.

[1]	Zhang　Yanmei, Yu　Haicun, Qiu　Qiuling. Effect of Solid Solution Process on the Organization and Mechanical Properties of 3Al-310S Heat-resistant Steel [J]. Special Steel, 2024, 45(6): 95-101.
[2]	Peng　Feng, Li　Xu, Li　Bopeng, Zhang　Yue, Wang　Zhanzhong, Guo　Shibei. Development of 10.9 Grade 32CrB4 Quenched and Tempered Round Steel for Fasteners [J]. Special Steel, 2024, 45(6): 8-11.
[3]	Zhao　Jiawei, Tian　Jialong, Yang　Ping, Zhan　Dongping, Jiang　Zhouhua. Effect of Dual-aging Process on Microstructure and Properties of Co-precipitation Hardening Ultra-high Strength Steel [J]. Special Steel, 2024, 45(6): 88-94.
[4]	Chen　Jun, Peng　Guangjian, Lin　Dan, Huang　Zhenhua. Production Practice of Ultra-Low Carbon Steel H1T in 150 mm×150 mm Small Billet [J]. Special Steel, 2024, 45(6): 17-22.
[5]	Yang　Wenbin, Liu　Zhongqiu, Wang　Fang, Huang　Xuechi, Lang　Yuping, Li　Baokuan. Effect of Melting Rate on Solidification Process of High Filled Ratio 06Cr18Ni11Ti Electroslag Remelting Ingot [J]. Special Steel, 2024, 45(6): 28-36.
[6]	Xie　Kang, Mo　Jinqiang, Zhang　Wei, Wang　Lijun. The Effect and Control of Rare Earth Ce on Carbonitrides Precipitation in 441 Ferritic Stainless Steel [J]. Special Steel, 2024, 45(6): 1-7.
[7]	Zhao　Guangdi, Zang　Ximin, Liu　Zhichao, Jing　Yu'an. Influence of Quenching Process on the Microstructure Evolution and Hardness of A514CrQ Rack Steel [J]. Special Steel, 2024, 45(6): 73-82.
[8]	Zhao　Haoqian, Zhang　Yuming, Ma　Bo, Gong　Yanjie, Meng　Yaoqing. Effect of LF Soft Bubbling Time on Inclusions in Tire Cord Steel LX82 A [J]. Special Steel, 2024, 45(6): 53-56.
[9]	Yuan lin, Hu Xiaoqiang, Liu Yang, Li Dianzhong, Xie Jing, Chen Wei. Comparative Analysis of 3%Cr Roller Steel by Rare Earth Refining and Electroslag Remelting [J]. Special Steel, 2024, 45(5): 1-7.
[10]	Li Qi, Qiu Guoxing, Wang Gongliang, Gao Peng, Li Rongxiang. Numerical Simulation of Bottom Argon Blowing Process for 130 Ton Ladle [J]. Special Steel, 2024, 45(5): 59-65.
[11]	Liu　Fubin, Jiang　Zhouhua, Li　Huabing, Feng　Hao, Dong　Junwei, Zhang　Quyi, Zheng　Huaibei. Development of Pressurized Electroslag Remelting Equipment and Process Technology [J]. Special Steel, 2024, 45(4): 26-33.
[12]	Zhang　Hong, Li Xu, Chen　Hua, Tang　Qing, Li　Linsen, Wang　Li, Gao　Shoulei. Effect of Heat Treatment Process on the Microstructure and Properties of 140 ksi Grade In718 Alloy [J]. Special Steel, 2024, 45(4): 139-145.
[13]	Jiang　Zhouhua, Dong　Yanwu, Liu　Fubin, Geng　Xin. The Latest Progress and Prospect of Special Metallurgical Products， Technology and Equipment in China [J]. Special Steel, 2024, 45(4): 1-12.
[14]	Dong　Liyang, You　Xiaogang, Dong　Gengyi, Wang　Yinong, Tan　Yi. The Metallurgical Mechanisms of Inclusions in the FGH4096 Alloy during Electron Beam Refining [J]. Special Steel, 2024, 45(4): 47-54.
[15]	Zhang　Donghai, Pan　Mingxu, Li　Xu, Xu　Yong, Xiong　Hao. Causes and Improvement of Point Defects in 15-5PH Stainless Steel Producted by EAF+VAR [J]. Special Steel, 2024, 45(4): 94-98.

Process Practice for Increasing Lining Life of 45 t AOD Units

提高45t AOD炉龄的工艺实践

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments