Research Progress on the Melting Process of Nickel-based Superalloy

doi:10.20057/j.1003-8620.2022-00200

Abstract

Abstract: The melting method of nickel-based superalloy is the decisive factor related to the alloy quality. Vacuum induction melting can effectively control the content of O， N， H and other gases and harmful impurities in alloy ingots， and accurately control the alloy composition. On this basis， the remelting of alloy （electroslag remelting and vacuum arc remelting） can further reduce the content of S， P and other harmful impurities， eliminate the defects such as component segregation and shrinkage cavity， and optimize the control of the solidification structure， so as to achieve the melting of large size and high-quality alloy ingots. This paper reviews the progress of the melting process of nickel-based superalloy， and focuses on the principles and characteristics of common melting technologies including vacuum induction melting， electroslag remelting， and vacuum arc remelting. The research progress of "vacuum induction melting + protective atmosphere electroslag remelting"， "vacuum induction melting + vacuum arc remelting" duplex melting process and "vacuum induction melting + protective atmosphere electroslag remelting + vacuum arc remelting" triple melting process in nickel-based superalloy melting are discussed. Finally， some suggestions on the selection and development direction of nickel-based superalloy smelting process are propounded.

Key words: Nickel-based Superalloy, Vacuum Induction Melting, Electroslag Remelting, Vacuum Arc Remelting, Duplex Melting Process, Triple-melting Process

摘要： 镍基高温合金的熔炼方法是合金质量的决定性因素，真空感应熔炼可有效控制合金锭中O、N、H等气体及有害杂质元素含量，精确控制合金成分。在此基础上，对合金进行重熔（电渣重熔及真空自耗重熔），可进一步降低合金中S、P等有害杂质含量，消除成分偏析及缩孔等缺陷，对凝固组织进行优化调控，从而实现大规格高质量合金锭的熔炼。本文综述了镍基高温合金的熔炼工艺进展，重点介绍了真空感应熔炼、电渣重熔、真空自耗重熔等常用熔炼技术的原理和特点，论述了“真空感应熔炼+保护气氛电渣重熔”、“真空感应熔炼+真空自耗重熔”双联工艺，以及“真空感应熔炼+保护气氛电渣重熔+真空自耗重熔”三联工艺在镍基高温合金熔炼方面的研究进展，并对镍基高温合金熔炼工艺的选择和发展方向提出建议。

关键词: 镍基高温合金, 真空感应熔炼, 电渣重熔, 真空自耗重熔, 双联工艺, 三联工艺

Yang　Hao, Wang　Fangjun, Li　Cai, Wu　Wei. Research Progress on the Melting Process of Nickel-based Superalloy[J]. Special Steel, 2023, 44(3): 1-9.

杨浩, 王方军, 李采, 吴畏. 镍基高温合金的熔炼工艺研究进展[J]. 特殊钢, 2023, 44(3): 1-9.

References

［1］ DebRoy T， Wei H L， Zuback J S， et al. Additive manufacturing of metallic components – Process， structure and properties［J］. Progress in Materials Science， 2018， 92： 112–224.
［2］ Hosseini E， Popovich V A. A review of mechanical properties of additively manufactured Inconel 718［J］. Additive Manufacturing， 2019， 30： 100877.
［3］王资兴. 三联冶炼工艺制备IN718合金棒材组织与性能控制［D］. 沈阳：东北大学， 2019.
［4］吴树森，吕书林. 有色金属熔炼入门与精通［M］. 北京：机械工业出版社， 2014： 271-273.
［5］付建辉，张健，赖宇. GH3128合金“VIM+ESR”和“NVIM+ESR”冶炼过程中的脱气行为及夹杂物研究［J］. 特殊钢， 2020， 41（6）： 15–19.
［6］ Gu D， Jia Q. Selective laser melting additive manufacturing of Inconel 718 superalloy parts： Densification， microstructure and properties［J］. Journal of Alloys and Compounds， 2014， 585： 713-721.
［7］ Reed R C. The Superalloys Fundamentals and Applications［M］. Cambridge： Cambridge university press， 2008： 421-426.
［8］ Zhang H K， Ma H C， Chang T X， et al. Deformation mechanisms of primary γ΄ precipitates in nickel-based superalloy［J］. Scripta Materialia， 2023， 224： 115109.
［9］李尧. 激光增材制造镍基高温合金DZ125L柱状晶等轴晶转变、热裂纹和再结晶的机理研究［D］. 西安：西安交通大学， 2018.
［10］姜兰. 用于镍基高温合金熔炼氧化锆耐火材料的研究［D］. 上海：上海大学， 2017.
［11］杨中卫，李涛，张曦东，等. 真空感应熔炼高牌号无取向硅钢的工艺试验［J］. 中国冶金， 2020， 30（8）： 21-24.
［12］金一标，李亚军，彭祺珉. 300 kg真空感应炉熔炼08Cr9CoMo钢的氧含量研究［J］. 特殊钢， 2021， 42（6）： 19-24.
［13］张勇，李佩桓，贾崇林，等. 变形高温合金纯净熔炼设备及工艺研究进展［J］. 材料导报， 2018， 32（9）： 1496-1506.
［14］李化坤，马中钢，逯红果，等. 镍基高温合金真空感应熔炼过程研究［J］. 山东冶金， 2020， 42（5）： 33-34.
［15］姜彩伟，刘建民，胡显军. 真空感应冶炼炉炉料架桥原因分析及改善措施［J］. 真空科学与技术学报， 2016， 36（12）： 1418-1421.
［16］赵鸿燕. 真空感应炉坩埚材质对镍基合金Inconel 690氧硫含量的影响［J］. 特殊钢， 2011， 32（6）： 43-46.
［17］ Qian K， Chen B， Zhang L， et al. Kinetics study of nitrogen removal from liquid IN718 alloy during vacuum induction melting［J］. Vacuum， 2020， 179： 109521.
［18］段生朝. 电渣重熔大型IN718镍基合金铸锭合金元素氧化控制的基础研究［D］. 北京：北京科技大学， 2021.
［19］ Ma C， Xia Z， Guo Y， et al. Carbides refinement and mechanical properties improvement of H13 die steel by magnetic-controlled electroslag remelting［J］. Journal of Materials Research and Technology， 2022， 19： 3272-3286.
［20］ Liu Y， Wang Y， Li G， et al. Investigation on the structure， fluoride vaporization and crystallization behavior of CaF₂–CaO–Al₂O₃–（SiO₂） slag for electroslag remelting［J］. Journal of Thermal Analysis and Calorimetry， 2020， 139（2）： 923-931.
［21］师帅. Inconel 740H镍基合金电渣重熔渣系及铸锭均质化的研究［D］. 沈阳：东北大学， 2018.
［22］李宝宽，黄雪驰，刘中秋，等. 现代电渣重熔先进技术特征与演进［J］. 钢铁， 2022， 57（6）： 1-11.
［23］彭龙生，刘春泉，周浩，等. 电渣重熔新技术的研究现状及发展趋势［J］. 材料导报， 2022， 36（S1）： 472-480.
［24］张勇，李佩桓，贾崇林，等. 变形高温合金纯净熔炼设备及工艺研究进展［J］. 材料导报， 2018， 32（9）： 1496-1506.
［25］ Cui J， Li B， Liu Z， et al. Comparative investigation on ingot evolution and product quality under different arc distributions during vacuum arc remelting process［J］. Journal of Materials Research and Technology， 2022， 18： 3991-4006.
［26］李莹莹. 大规格钛合金真空自耗铸锭热封顶技术探讨［J］. 特种铸造及有色合金， 2020， 40（3）： 324-326.
［27］ Karimi-Sibaki E， Kharicha A， Wu M， et al. A Parametric Study of the Vacuum Arc Remelting （VAR） Process： Effects of Arc Radius， Side-Arcing， and Gas Cooling［J］. Metallurgical and Materials Transactions B， 2020， 51（1）： 222-235.
［28］ Huang X， Li B， Liu Z. Three-Dimensional Mathematical Model of Oxygen Transport Behavior in Electroslag Remelting Process［J］. Metallurgical and Materials Transactions B， 2018， 49（2）： 709-722.
［29］姜周华. 电渣治金学［M］. 北京：科学出版社， 2015： 255-257.
［30］陈韩锋，张东. 气氛保护电渣重熔GH4169的冶金质量及锻造性能分析［J］. 甘肃科技， 2021， 37（7）： 53-57.
［31］贾景岩，练明生，曹海洋. 氩气保护电渣重熔GH2132提高Ti收得率实践［J］. 中国金属通报， 2021（8）： 162-163.
［32］陈国胜，周奠华，金鑫，等. 全封闭Ar气保护电渣重熔GH4169合金［J］. 特殊钢， 2004，24（3）： 46-47.
［33］刘立，赵俊学，李献民，等. CaF2-CaO-Al2O3-SiO2-MgO五元渣的表面张力及其在镍基合金电渣重熔的应用［J］. 特殊钢， 2015， 36（6）： 20-22.
［34］崔利民，王忠鑫，罗保帅，等. GH2132合金2 t 电渣锭重熔工艺改进［J］. 特殊钢， 2022， 43（3）： 43–46.
［35］ Duan S C， Shi X， Zhang M C， et al. Effect of Slag Composition on the Deoxidation and Desulfurization of Inconel 718 Superalloy by ESR Type Slag Without Deoxidizer Addition［J］. Metallurgical and Materials Transactions B， 2020， 51（1）： 353–364.
［36］ Radwitz S， Scholz H， Friedrich B， et al. Process and Refining Characteristics of ESR using MgO containing Slag Systems［C］. Leoben： International Symposium on Liquid Metal Processing and Casting， 2015.
［37］王资兴，王磊，孙文儒. 熔速对IN718合金真空自耗铸锭组织的影响［J］. 材料热处理学报， 2019， 40（1）： 91–97.
［38］ Davidson P A， He X， Lowe A J. Flow transitions in vacuum arc remelting［J］. Materials Science and Technology， Taylor & Francis， 2000， 16（6）： 699–711.
［39］于腾，杨玉军，宋彬，等. 真空电弧重熔过程中白斑缺陷的成因分析［J］. 金属功能材料， 2022， 29（2）： 28-33.
［40］ Wang X， Ward R M， Jacobs M H， et al. Effect of Variation in Process Parameters on the Formation of Freckle in INCONEL 718 by Vacuum Arc Remelting［J］. Metallurgical and Materials Transactions A， 2008， 39（12）： 2981-2989.
［41］郭建亭. 高温合金材料学［M］. 北京：科学出版社， 2008： 103-105.
［42］杨玉军，李爱民，赵长虹，等. 氦气冷却对高温合金真空自耗重熔的影响［C］. 北京：中国金属学会高温材料分会， 2007： 20-23.
［43］赵长虹，张玉春，杨玉军，等. 真空自耗锭生产工艺对GH4169合金组织和力学性能的影响［C］. 北京：中国金属学会高温材料分会， 2007： 131-134.
［44］ II’inskii A I， Livatkin P A， Polozhentsev K A. Effectiveness of a new automated control system for vacuum-arc remelting［J］. Steel in Translation， 2015， 45（11）： 825-829.
［45］ Chen Z， Yang S， Qu J， et al. Effects of Different Melting Technologies on the Purity of Superalloy GH4738［J］. Materials， 2018， 11（10）： 1838-1840.
［46］陈国胜，刘丰军，王庆增，等. GH4169合金VIM+PESR+VAR三联冶炼工艺及其冶金质量［J］. 钢铁研究学报， 2011， 23（S2）： 134-137.
［47］张勇，李鑫旭，韦康. 三联熔炼GH4169合金大规格铸锭与棒材元素偏析行为［J］. 金属学报， 2020， 56（8）： 1123-1132.
［48］王晓峰，周晓明，穆松林，等. 高温合金熔炼工艺讨论［J］. 材料导报， 2012， 26（7）： 108-113.
［49］高小勇. FGH96粉末高温合金母合金的纯净化技术研究［D］. 北京：北京科技大学， 2020.
［50］胡连喜，冯小云. 粉末冶金高温合金研究及发展现状［J］. 粉末冶金工业， 2018， 28（4）： 1-7.
［51］庄景云. 变形高温合金GH4169［M］. 北京：冶金工业出版社， 2006； 42-44.
［52］阚志，吴贵林，于腾，等. GH4706合金超大尺寸棒材冶炼及加工工艺研究［C］. 北京：第十三届中国高温合金年会，中国金属学会高温材料分会， 2015： 125-127.
［53］ Loria E A.Superalloy 718，625，706 and various derivatives［M］. Warrendale，Pennsylvania：TMS，2005：15-17.

[1]	Ni　Zhuowen, Zhu　Hongchun, Li　Huabing, Jiang　Zhouhua, Sun　Zhengxin, He　Zhiyu. Analysis of the Types and Distribution of Inclusions in H13 Die Steel Electroslag Ingots [J]. Special Steel, 2024, 45(6): 48-52.
[2]	Yang　Wenbin, Liu　Zhongqiu, Wang　Fang, Huang　Xuechi, Lang　Yuping, Li　Baokuan. Effect of Melting Rate on Solidification Process of High Filled Ratio 06Cr18Ni11Ti Electroslag Remelting Ingot [J]. Special Steel, 2024, 45(6): 28-36.
[3]	Yuan lin, Hu Xiaoqiang, Liu Yang, Li Dianzhong, Xie Jing, Chen Wei. Comparative Analysis of 3%Cr Roller Steel by Rare Earth Refining and Electroslag Remelting [J]. Special Steel, 2024, 45(5): 1-7.
[4]	Wang　Bingjie, Wang　Yu, Xiang　Miaomiao, Shi　Xiaofang, Chang　Lizhong. Effect of Current Intensity on the Cleanliness of Electroslag Ingots During Low Frequency Electroslag Remelting [J]. Special Steel, 2024, 45(4): 77-82.
[5]	Cao　Yulong, Zhang　Saikang, Wang　Xiuxiu, Ma　Chongsheng, Li　Guangqiang. Effect of Heating Temperature on Decomposition Transition Behavior of M₂C Carbide in High-vanadium High-speed Steel [J]. Special Steel, 2024, 45(4): 146-152.
[6]	Yang　Shulei, Wang　Xiwei, Tian　Qiang, Wang　Tiantian, Yang　Shufeng. Distribution Characteristics of Inclusions in GH4742 Superalloy Ingot by Vacuum Arc Remelting [J]. Special Steel, 2024, 45(4): 61-67.
[7]	Zhao　Zimin, Sun　Xin, Hou　Dong, Zhou　Weiji, Yao　Yudong, Sun　Changliang. Transformation of the Completely Enclosed Atmosphere in Ordinary Electroslag Furnace and Its Influence on Typical Steel Grades [J]. Special Steel, 2024, 45(4): 99-103.
[8]	Zhou　Yang, Zhu　Hongchun, Li　Huabing, Jiang　Zhouhua, He　Zhiyu, Ni　Zhuowen. Simulation of Columnar Crystal Growth in Forced Flow of VAR Based on Phase Field Method [J]. Special Steel, 2024, 45(4): 41-46.
[9]	Sun　Zhonghao, Li　Qiang, Zhang　Mingliang, Ma　Chengkuan, Xia　Zhibin, Zhong　Yunbo. Effect of Magnetic-Controlled Electroslag Remelting on Solidification Microstructure and Mechanical Properties of M2 High-speed Steel [J]. Special Steel, 2024, 45(4): 68-76.
[10]	Zhao　Peng, Gui　Kaixuan, Qu　Jinglong, Yang　Shufeng. Numerical Simulation and Industrial Experiment of Vacuum Arc Remelting ϕ690 mm Large-sized GH4738 Superalloy Ingot [J]. Special Steel, 2024, 45(4): 55-60.
[11]	Liu　Fubin, Jiang　Zhouhua, Li　Huabing, Feng　Hao, Dong　Junwei, Zhang　Quyi, Zheng　Huaibei. Development of Pressurized Electroslag Remelting Equipment and Process Technology [J]. Special Steel, 2024, 45(4): 26-33.
[12]	Gao　Xiaoyong, Zhang　Lifeng. Effect of Electroslag Remelting Using 37 Slag on Inclusions in M50 High-temperature Bearing Steel [J]. Special Steel, 2024, 45(4): 89-93.
[13]	Fan　Xiaoshuo, Liu　Yufeng, Yuan　Hua. Effect of Powder Treatment on Oxygen Content， Microstructure and Mechanical Properties of FGH95 Superalloy [J]. Special Steel, 2024, 45(4): 124-130.
[14]	Peng　Leizhen, Jiang　Zhouhua, Shen　Guoqu, Geng　Xin, Qiu　Guoxing, Wang　Cheng. Oxidation Behavior of Electrode Surface and Deoxidation System During Electroslag Remelting 9CrMoCoB Steel [J]. Special Steel, 2023, 44(6): 70-77.
[15]	Li　Longfei, Lin　Tengchang, Zhang　Qiang, He　Xikou, Chen　Zhengzong , Zhou　Xiaozhou. The Effect of Electroslag Remelting Slag System on Inclusions in C-HRA-3 Heat-Resistant Alloy [J]. Special Steel, 2023, 44(5): 76-82.